Abstract:Enhancing the fire safety of epoxy resins (EPs) typically requires a significant amount of flame retardants, which often results in considerable degradation of their mechanical properties. To address this issue, a novel flame retardant known as PDCP@DPA@MXene was synthesized and integrated into EP to achieve notable improvements in flame retardancy, smoke suppression, and mechanical strength. By incorporating 1.5 wt% PDCP@DPA@MXene, the impact strength, tensile strength, and elongation at break of the resulting PDM-1.5 %/EP composite reached 12.1 kJ/m2, 57.4 MPa, and 13.0, respectively, reflecting enhancements of 63.5 %, 18.4 %, and 17.1 % compared to the pure EP. The enhancement in tensile strength may be attributed to the high rigidity of Ti3C2Tx MXene, which reinforces the EP matrix. Additionally, the intertwined structure of PDCP@DPA@MXene chains effectively mitigates material fracturing and absorbs impact forces, thus toughening the EP. The presence of phosphorus, nitrogen, and titanate in PDCP@DPA@MXene contributes to the formation of a more compact char layer. The PDM-1.5 %/EP sample achieved a V-0 rating in the vertical UL-94 test and exhibited a high limiting oxygen index of 32.0. Furthermore, the sample containing 2 wt% PDCP@DPA@MXene showed a significant reduction in peak heat release rate (p-HRR) and total heat release (THR), recording values of 689 kW/m2 and 71.9 MJ/m2, which are decreases of 45.1 % and 26.9 %, respectively, compared to pure EP. Additionally, the incorporation of PDCP@DPA@MXene led to a reduction in CO production. These flame-retarded EPs demonstrate strong potential for various applications due to their elevated glass transition temperature and robust thermal stability.

Siloxane-decorated MXene nanosheet-reinforced EP composites with outstanding flame retardancy and liquid-oxygen compatibility for ultra-low-temperature applications

Surface modification of MXene nanosheets with P-N-containing agents for boosting flame retardancy of epoxy resin

Linear polydichlorophosphazene and Ti3C2Tx MXene nanohybrids: Synthesis and application to epoxy resin to improve the fire safety and mechanical properties

Fire-safe epoxy composite realized by MXenes based nanostructure with vertically arrayed MOFs derived from interfacial assembly strategy

Hydrogen bonding induced polyphosphazene/MXenes 2D/2D structure loaded with MOFs enabling fire-safe epoxy composite

Functionalizing mesoporous silica with a nano metal–organic phosphonate towards mechanical‐robust, thermal‐resistant, and fire‐safety epoxy resin

A Bifunctional Modifier Endowing Epoxy Resin with Outstanding Flame Retardancy and High Impact Strength

Improving Fire Resistance of Epoxy Resin Using Electrolytic Manganese Residue-Based Zeolites Modified with Metal–organic Framework Ligands

Functionalized halloysite nanotubes endowing epoxy resin with simultaneously enhanced flame retardancy and mechanical properties

Novel exploration of the flame retardant potential of bimetallic MXene in epoxy composites

Inspired by placoid scale to fabricate MXene derivative biomimetic structure on the improvement of interfacial compatibility, mechanical property, and fire safety of epoxy nanocomposites

In-situ encapsulated MXene nanosheets with bimetallic phosphate: towards for reducing the fire risk of epoxy composites

Ionic liquids modified MXene as a flame retardant synergist for the unsaturated polyester resin

A multifunctional epoxy composites based on cellulose nanofiber/carbon nanotube aerogels: Simultaneously enhancing fire-safety, thermal conductive and photothermal performance

Facile fabrication of low-content surface-assembled MXene in silicone rubber foam materials with lightweight, wide-temperature mechanical flexibility, improved flame resistance and exceptional smoke suppression

Construction of Multifunctional Linear Polyphosphazene and Molybdenum Diselenide Hybrids for Efficient Fire Retardant and Toughening Epoxy Resins

Anomalous Nano-Barrier Effects of Ultrathin Molybdenum Disulfide Nanosheets for Improving the Flame Retardance of Polymer Nanocomposites

Facile fabrication of novel fire-safe MXene@IL-based epoxy nanocomposite coatings with enhanced thermal conductivity and mechanical properties

Heterostructured Graphene@Silica@Iron Phenylphosphinate for Fire-Retardant, Strong, Thermally Conductive Yet Electrically Insulated Epoxy Nanocomposites

Novel Phosphorus-Nitrogen-Containing Ionic Liquid Modified Metal-Organic Framework as an Effective Flame Retardant for Epoxy Resin