Abstract:The MgAl layered hydrotalcites (MgAl-LDHs) precursors with submicron-scale were synthesized by introducing ethanol into hydrothermal synthesis method. The synthesis process parameters were optimized by orthogonal experiment, and then the composite metal oxide (MgAlOx) was obtained after the calcination process. The crystal phase, morphology and alkalinity of both hydrotalcite precursors and solid base oxides were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and the temperature-programmed desorption of CO2(CO2-TPD), respecitively. Finally, the catalytic performance of MgAlOx was evaluated by the depolymerization test of calcium lignosulfonate. The products including solid, liquid, gas three phases, were analyzed by gel permeation chromatography (GPC), gas chromatography/mass spectrometry (GC-MS) and gas chromatography (GC). The results indicated that 140-230 nm of MgAl-LDHs were regulated by adding 15% (volume fraction) C2H5OH to the hydrothermal system, the optimal synthesis condition considered from relative crystallinity was n(Mg)/n(Al)=3, pH=12 and the temperature of 80 degrees C for 24 h. the MgAlOx obtained after the calcination of MgAl-LDHs at 600 degrees C for 6 h under air atmosphere. The optimal depolymerization of calcium lignosulfonate was 270 degrees C, 4 h, the addition of 65% (volume fraction) C2H5OH and m(MgAlOx)/m(CLS)=1/2. The gas-liquid-solid three-phase yield distribution was 4.50%, 58.30% and 37.20% under the above condition, the liquid yields increased by 13.30% with the addition of MgAlOx, the main components of liquid products were phenolics, aromatics, esters and others. Moreover, the selectivity of oxy-containing compounds was 79.05% (phenolics of 66.06%, esters of 12.99%). Fortunately, MgAlOx would also keep high reactivity and stability even after four cycles of reactions.

MATERIALES MESOPOROSOS TIPO HIDROTALCITA OBTENIDOS POR SOL-GEL ASISTIDO CON IRRADIACIÓN DE MICROONDAS Y SU EVALUACIÓN CATALÍTICA Y ADSORBENTE HYDROTALCITE-LIKE MESOPOROUS MATERIALS OBTAINED BY THE SOL - GEL METHOD WITH MICROWAVE RADIATION AND HIS EVALUATION AS CATALISTS AND SORBENT

Mesoporous MgTa 2o 6 thin films with enhanced photocatalytic activity: On the interplay between crystallinity and mesostructure

Synthesis of Mg-Al Hydrotalcite Clay with High Adsorption Capacity

Preparation of Mesoporous Analcime/Sodalite Composite from Natural Jordanian Kaolin

Synthesis Of Mg-Zn-Al Hydrotalcites-Like And Catalytic Activities Of Their Composite Oxides

Influence Of The Synthesis Method Of Layered Double Hydroxides On The Textural Properties And Nitrate Removal

Production of Oxygen-containing Compounds Catalytic from Depolymerization of Calcium Lignosulphonate by Submicron-scale MgAl Solid Base

Microemulsion Templating Synthesis of Hierarchical Porous Ag‐Doped SiO2‐TiO2 Composites for Efficient Degradation of Noxious Methylene Blue Dye: Effect of Calcination Environment

Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media

Catalytic Activities and Properties of Mesoporous Sulfated Al2O3–ZrO2

Evaluation of the Behavior of Hydrotalcite Like-Materials for CO2 Capture

Photocatalytic degradation of 2,4-dichlorophenol with MgAlTi mixed oxides catalysts obtained from layered double hydroxides

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Synthesis of Porous MgAl-LDH on a Micelle Template and Its Application for Efficient Treatment of Oilfield Wastewater

Tailoring the Surface of Sintered Magnesia–Chromia Catalyst with a Sol–Gel Auto-Combustion Technique

Micro to mesoporous SiO2xerogels: the effect of acid catalyst type in sol–gel process

Catalytic activities and properties of mesoporous sulfated Al 2 O 3 –ZrO 2

Innovative Synthetic Approaches for Sulphate-Promoted Catalysts for Biomass Valorisation

Ordered Mesoporous Materials with Improved Stability and Catalytic Activity

ChemInform Abstract: Hydrothermal—Thermal Conversion Synthesis of Hierarchical Porous MgO Microrods As Efficient Adsorbents for Lead(II) and Chromium(VI) Removal.

Synthesis of γ-Al2O3–CeO2 catalyst with high surface area, high stability, and less coke formation for methanol dehydration reaction process