Abstract:Due to the rapid heating-cooling process and unstable keyhole, pore defects are easily formed during the high energy beam-powder additive manufacturing (AM) process, posing great challenges to the high-performance manufacturing of aerospace components. Using an arc with lower energy density as a heat source can effectively avoid these defects, but its matching raw materials are limited to wire. In this paper, a novel magnetic field assisted powder arc additive manufacturing (MFA-PAAM) method has been proposed, which combines arc heat source and powder raw material to achieve dense metal parts. A transverse magnetic field (TMF) was introduced to solve the powder spattering problem which impacts the stability of the PAAM process, by regulating the direction of the arc plasma flow and the arc pressure. The unique melting behavior of the powder under arc heating was captured by a high-speed camera, which can be summarized into two steps: balling and adsorption by the molten pool. And the well-formed and fully dense Ti60 high-temperature titanium alloy wall components were successfully manufactured using the self-developed equipment. The microstructure of the thin-wall component is dominated by basket-weave distributed α laths and few β sheets remaining at their boundaries. A layered periodic distribution along the building direction was observed, which is mainly distinguished from the content and morphology of the β phase. The average ultimate tensile strength (UTS) and elongation to failure in the travelling direction are 1003.2 MPa and 15.1%, while the average UTS and elongation along the building direction are 1009.3 MPa and 16.6%, respectively. The fracture morphologies in both directions are characterized by ductile fracture. The MFA-PAAM technique shows great potential for fabricating materials that are difficult to be drawn into wires with high efficiency and performance.

Large area hole defect repair of titanium alloys by powder pressing and vacuum sintering

Microstructure and tensile properties of transient liquid phase (TLP) sintering repaired Ti-6Al-4V alloys with large area hole defect

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Integrated high-performance and accurate shaping technology of low-cost powder metallurgy titanium alloys: A comprehensive review

Micro-mechanism and mechanical properties of solid-powder hot isostatic pressing diffusion-bonded Ti2AlNb alloy

Achieving synergy of strength and ductility in powder metallurgy commercially pure titanium by a unique oxygen scavenger

Investigating phase transformation, densification and diffusion mechanism of TiH 2 powder to achieve a high ductile Ti6Al4V alloy

Achieving excellent strength-ductility combination in Ti–6Al–4V alloy by spark plasma sintering technology using large-diameter PREP spherical powder

Fabrication of Ti3Al-Based Intermetallic Alloy by Laser Powder Bed Fusion Using a Powder Mixture

In-situ tensile deformation behavior of powder metallurgy Ti6Al4V alloys

A novel magnetic field assisted powder arc additive manufacturing for Ti60 titanium alloy: Method, microstructure and mechanical properties

Microstructure and Interfacial Reactions of Resistance Brazed Lap Joints between TC4 Titanium Alloy and 304 Stainless Steel Using Metal Powder Interlayers

Preparation of Spherical Porous and Spherical Ti6Al4V Powder by Copper-Assisted Spheroidization Method

A Method for the Preparation of Spherical Titanium Powder for Additive Manufacturing

Formation and evolution mechanisms of micropores in powder metallurgy Ti alloys

Phase Transformation, Microstructural Evolution and Tensile Properties of a TiH2-Based Powder Metallurgy Pure Titanium

Laser metal deposition of titanium on stainless steel with high powder flowrate for high interfacial strength

Plasma Transferred Arc Powder Surfacing for Titanium-Clad Steel Plate

Developing ductile and isotropic Ti alloy with tailored composition for laser powder bed fusion

Synergistic Improvement in Ductility and Hot Nitric Acid Corrosion Resistance of LPBF Ti-6Al-4V Alloy via Hot Isostatic Pressing

Densification behavior, mechanical and electrical properties of in-situ TiB 2p /Cu composite powder via vacuum hot pressing