Abstract:In a hypervelocity impact (HVI) between the micrometeoroids/orbital debris (MMOD) and multi-layered shielding mechanisms of spacecraft, the debris cloud, formed by shattered materials of the outer bumper layer and projectile, commits multitudinous pitting craters and cracks that are disorderedly scattered in the rear wall layer. Material degradation due to the pitting damage is a precursor of structural fragmentation and system failure of the space assets. In this study, microscopic material degradation of the rear wall of a typical dual-layered Whipple shield, initiated and intensified by the debris cloud-engendered pitting damage, is characterized using metallographic analysis including optical microscope (OM), laser scanning microscope (LSM), scanning electron microscope (SEM) and X-ray diffraction (XRD). Results have revealed that (1) the degree of material degradation shows difference in the central cratered area, the ring cratered area, and the spray area, respectively; (2) the dynamic recrystallization gives rise to the formation of fine grains adjacent to pitting craters; (3) the extents of recrystallization and dislocation depend on the strain rate levels during HVI; and (4) the temperature elevation, caused by the heat transformed from the adiabatic plastic deformation energy and shock heating, warrants the recrystallization. Two types of damage, namely micro-voids and micro-cracks, are identified beneath the pitting damage area; under the extremely high compressive strain rate induced by HVI, micro-voids are initiated by the nucleation of grains or deteriorate from existing material defects, and these micro-voids further expand at the grain boundaries and within the grains to form micro-cracks under a tensile-type wave converted from the HVI-induced shock wave.

Failure evolution in hypervelocity impact of Al spheres onto thin Al plates

Analysis of the stress wave and rarefaction wave produced by hypervelocity impact of sphere onto thin plate

Damage Characteristics of Aluminum Nanorod under Hypervelocity Impact

On Propagation of Shock Waves Generated under Hypervelocity Impact (hvi) and Application to Characterizing Orbital Debris-Induced Damage in Space Vehicles

Analysis on the fragmentation pattern of sphere hypervelocity impacting on thin plate

Influence of the impedance gradient on the debris cloud produced by hypervelocity impact

Impact Crushing and Rebound of Thin-Walled Hollow Spheres

Investigation on Damage Characteristics of Thin Al-Plates by Oblique Hypervelocity Impact of Al-Sphere

Study on damage mechanism and damage distribution of the rear plate under impact of debris cloud

Numerical investigation of hypervelocity impact simulation with FEM/SPH formulation for space structures

Numerical study on the phase-transition characteristics of debris cloud under hypervelocity impacts

Modeling on Propagation of Shock Waves Induced by Hypervelocity Impact (hvi) with Application to Evaluation of Hvi Damage

Three-dimensional Characterization of Debris Clouds under Hypervelocity Impact with Pulsed Digital Inline Holography.

Hypervelocity Impact Detection and Location for Stiffened Structures Using a Probabilistic Hyperbola Method

Size investigation of hole due to hypervelocity impact aluminum spheres on thin aluminum sheet

Microstructural Material Characterization of Hypervelocity-Impact-induced Pitting Damage

Predicting the Damage on a Target Plate Produced by Hypervelocity Impact Using a Decoupled Finite Particle Method

Modeling Hypervelocity-Impact-Induced Shock Waves for Characterizing Orbital Debris-Produced Damage

The damage characteristics and formation mechanism of ultrahigh strength 7055 aluminum alloy under hypervelocity impact

Experimental investigation for deformation and fragmentation of spheres penetrating sheets at hypervelocity

Damage of Al-Whipple Shield Rear Wall Caused by Hypervelocity Impact of Al-spheres