Abstract:This study investigated the microstructure, residual stress, and fatigue behavior of duplex stainless steels that have been annealed with different annealing processes. A cold-rolled AISI 2205 Duplex Stainless Steel (DSS) sample was annealed in three ways for this purpose. In modes 1 and 2, samples were annealed at 500°C for 6 and 8 hours, respectively. The sample was annealed for 6 hours at 950°C for mode 3.The Optical Microscopy (OM) technique was used to determine the crystallographic texture and microstructural characteristics. An X-ray Diffraction (XRD) analysis was used to determine the residual stresses in austenite and ferrite phases on pre- and post-heat-treated samples. The Scanning Electron Microscope (SEM) technique was utilized to assess fatigue cracks. The results showed that the texture microstructure of the specimens using mode 1 and 2 were remained; the grain had a smaller fragmentation. The elongation grains of the specimen after mode 3 were smaller, relatively spheroidal, and more homogeneous. There was a reduction in residual stress after mode 3 annealing process. The fatigue strength of the specimens that under applied this process was 11.1% higher than that of specimens in the as-received state. On examine encore le traitement thermique pour améliorer les propriétés mécaniques de l'acier, puisque c'est un procédé complexe qui a besoin d'être étudié en profondeur. Dans l'étude en cours, on a réalisé une étude de la microstructure, des contraintes résiduelles et du comportement à la fatigue des aciers inoxydables duplex qui one été recuits avec différents traitements de recuit. Dans cette étude, on a recuit de trois façons des échantillons laminés à froid d'acier inoxydable duplex (DSS) AISI 2205. Dans les modes 1 et 2, on a recuit les échantillons à 500°C pendant 6 et 8 heures, respectivement. Pour le mode 3, on a recuit les échantillons pendant 6 heures à 950°C. La technique de microscopie optique (MO) a déterminé la texture cristallographique et les caractéristiques microstructurales. On a utilisé une analyse de diffraction des rayons X (XRD) pour déterminer les contraintes résiduelles dans les phases d'austénite et de ferrite des échantillons pré- et post-traités thermiquement. La technique du microscope électronique à balayage (MEB) a évalué les fissures de fatigue. Les résultats ont montré que la texture de la microstructure des spécimens utilisant les modes 1 et 2 demeurait en place; le grain présentait une plus petite fragmentation. Les grains allongés des spécimens après le mode 3 étaient plus petits, relativement sphériques et plus homogènes. Il y avait une réduction de la contrainte résiduelle après le procédé de recuit du mode 3. La résistance à la fatigue des spécimens qui ont subi ce procédé était de 11.1% supérieure à celle des spécimens à l'état tel que reçu.

Effect of hot coil immersion cooling process on microstructure and properties of strip steel and oxide scales

Effect of Cooling Rate on Microstructure Evolution and Mechanical Properties of SCM435 Steel

Effect of microstructure and microtexture evolution of oxide layer over J82B steel on mechanical descaling properties

Effect of Cooling Process on Microstructure and Mechanical Properties of Hot Rolled 65Mn Steel

Influence of warm rolling temperature on multi-scale lamellar structure and mechanical properties of medium carbon steel

Effect of cooling route on microstructure and mechanical properties of twin-roll casting low carbon steels with an application of oxide metallurgy technology

Influence of Cooling Process on Microstructure and Property of Low-Carbon V–N Micro-alloyed Medium and Heavy High-Strength Steel Plate

Effects of Warm Temper Rolling on Microstructure, Texture and Magnetic Properties of Strip-Casting 6.5wt% Si Electrical Steel

Effect of Rolling Temperature and Ultrafast Cooling Rate on Microstructure and Mechanical Properties of Steel Plate

An Investigation of Friction Coefficient on Microstructure and Texture Evolution of Interstitial-Free Steel during Warm Rolling and Subsequent Annealing

Study on hot compressive deformation behavior and microstructure evolution of G13Cr4Mo4Ni4V steel

Microstructure evolution and compressive properties of a low carbon-low alloy steel processed by warm rolling and subsequent annealing

Effect of Cooling Rate on Microstructure and Mechanical Properties of a Microlaminated Low-Density Steel

Structural transformation behavior of oxide scale during coiling of 0.9 wt% Cr-containing high-strength steel

Effect of Cooling Rates on the Local—Overall Morphology Characteristics of Solidification Structure at Different Stages for High Carbon Steel

Effect of annealing process on microstructure, residual stress, and fatigue behaviour of AISI 2205 duplex stainless steel

Importance of cold rolling and tempering on the microstructure evolution, precipitation behavior and mechanical responses of 9Cr3Co3W1Cu ferritic/martensitic steel

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Optimization of Annealing Parameters for Ferritic Hot-Rolled IF Grade Steel

Effects of rolling temperature on microstructure, texture, formability and magnetic properties in strip casting Fe-6.5wt% Si non-oriented electrical steel

Microstructural Analysis and Hardening Mechanism of High-Strength Low-Carbon Weathering Steel: Effect of Coiling Temperature