Abstract:In this paper, salt spray tests were firstly conducted for Q690 high strength steel plates. After the corrosion tests, the corrosion products were removed and the weight loss ratio was obtained. Then the topographies of the rough surfaces were scanned by a 3D surface profiler, and the 3D coordinates of the corroded surfaces were exported. Based on the data, the topographic feature parameters were determined, the uniform corrosion depth was calculated, and the extreme value analysis was conducted for the pitting corrosion depth to investigate its stochastic features. Finally, the corroded surfaces were restored and the finite element models of the scanned segments were established, which were validated by the experimental results and used to conduct the stress concentration analysis. The experimental results showed that the topographic feature parameters were linearly related to the weight loss ratio, and the maximum pitting depth conformed to the Frechat distribution. By conducting finite element analysis, it was concluded that under the uniaxial tensile load, the corroded steel plate showed an obvious stress concentration effect and most nodes were in a multiaxial stress state. In terms of the characteristic loads, both uniform and pitting corrosion induced the yield load and the ultimate load degradation. Regarding the uniform corrosion component, the loss percentage of the characteristic load was equal to the corresponding weight loss ratio. However, the loss percentages of the characteristic loads caused by pitting corrosion were smaller than the pitting weight loss ratio due to the stress concentration.

Elastic stress impacting on the rust layer of S450EW weathering steel through magnetomechanical effect

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Rusting behavior of a deformed 450 MPa-grade weathering steel in 5 wt.% NaCl salt spray

Study On Modulus Of Rust Applied In Steel Corrosion Induced Concrete Cracking Model

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Experimental study on stress detection of corroded steel bars based on piezomagnetic effect

Experimental study and finite element analysis of degradation behavior of epoxy zinc-rich coating system under stress corrosion

Mechanical Performance of Artificially Rusted Q500MC Structural Steel Subjected to High Temperature

EXPERIMENTAL STUDY OF PIEZOMAGNETISM OF PITTING CORROSIONSTEEL BARS UNDER TENSILE FORCE

Strength degradation of a ferrite-bainite weathering steel subjected to corrosion fatigue environment

Characterization of the Rust Formed on Weathering Steel Exposed to Qinghai Salt Lake Atmosphere

Mechanism in the Effect of External Stresses on the Oxidation and Scale Growth Kinetic of Steels under Cyclic Temperatures

Surface topography and stress concentration analysis for corroded high strength steel plate

The influence of tensile stress on the electrochemical behavior of X80 steel in a simulated acid soil solution

CORROSION BEHAVIOR OF WEATHERING STEEL IN A WET/DRY ENVIRONMENT CONTAINING MgCl2

Degradation Damage of Stress Corrosion in Epoxy Zinc-Rich Coating/Steel Substrate Systems

INFLUENCE OF TENSILE STRESS ON EXFOLIATION CORROSION AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF 7075al - ALLOY

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: Initial corrosion with tensile stress coupling

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

The Effect of Applied Tensile Stress on the Exfoliation Corrosion of 7075‐T6 Alloy

Synergy of stress and corrosion in a 12Cr ferritic/martensitic steel exposed to static liquid lead-bismuth eutectic at 550°C