Abstract:Bleached bamboo pulp, as a kind of natural cellulose, has received significant attention in the field of biomass materials due to its advantages of environmental protection and the abundance of raw materials. Low-temperature alkali/urea aqueous system is a green dissolution technology for cellulose, which has promising application prospects in the field of regenerated cellulose materials. However, bleached bamboo pulp, with high viscosity average molecular weight (Mη) and high crystallinity, is difficult to dissolve in an alkaline urea solvent system, restraining its practical application in the textile field. Herein, based on commercial bleached bamboo pulp with high Mη, a series of dissolvable bamboo pulps with suitable Mη was prepared using a method of adjusting the ratio of sodium hydroxide and hydrogen peroxide in the pulping process. Due to the hydroxyl radicals being able to react with hydroxyls of cellulose, molecular chains are cut down. Moreover, several regenerated cellulose hydrogels and films were fabricated in an ethanol coagulation bath or a citric acid coagulation bath, and the relationship between the properties of the regenerated materials and the Mη of the bamboo cellulose was systematically studied. The results showed that hydrogel/film had good mechanical properties, as the Mη is 8.3 × 104 and the tensile strength of a regenerated film and the film have values up to 101 MPa and 3.19 MPa, respectively. In this contribution, a simple method of a one-step oxidation of hydroxyl radicals to prepare bamboo cellulose with diversified Mη is presented, providing an avenue for a preparation of dissolving pulp with different Mη in an alkali/urea dissolution system and expanding the practical applications of bamboo pulp in biomass-based materials, textiles, and biomedical materials.

Effect of hemicellulose content on the solution properties of cellulose carbamates in NaOH/ZnO aqueous system

The Effects of NaOH-Urea Aqueous Solution on the Strength and Softness Properties of Bamboo Ligno-cellulosic Fibers

Cellulose Nanowhiskers from Moso Bamboo Residues: Extraction and Characterization

Modification on the Chemi-mechanical Pulping Property of Rice Straw with Alkali-urea System

MICRO-CELLULOSE PREPARATION METHOD BASED ON UREA/NaOH DISSOLVED SYSTEM

One-Step Treatment for Upgrading Bleached Bamboo Pulp to Dissolving Pulp High Solvency in Green Alkali/Urea Aqueous Solution

Solubility of Cellulose in NaOH/Urea Aqueous Solution

Cellulose dissolution in aqueous NaOH–ZnO: effect of pulp pretreatment at macro and molecular levels

Effect of the Dissolving Method on the Dissolution of Dissolving Pulp Cellulose Fibers with Different Dried-States in Different NaOH/Additives Aqueous Solutions

Dissolution of cellulose from different sources in an NaOH/urea aqueous system at low temperature

Role of Sodium Zincate on Cellulose Dissolution in NaOH/urea Aqueous Solution at Low Temperature

Synthesis of High Quality Carboxymethyl Cellulose by Bamboo Pulp

Participation of sodium sulfamate as hydrogen bond-donating and hydrogen bond-accepting additive in the dissolution of cellulose in NaOH aqueous solution

Preparation of NaOH-H2O2 Cotton Viscose Pulp with Cellulase Post-treatment

Hydrolysis of cellulose of bamboo fiber during dissoultion

Efficient separation of cellulose from bamboo by organic alkali

Preparation of NaOH-H_2O_2 Cotton Viscose Pulp with Cellulase Posttreatment

Improved Cellulose Yield in the Production of Dissolving Pulp from Bamboo Using Acetic Acid in Prehydrolysis

Hemicellulosic Derivatives With Cationic Groups As Wet End Additives In Papermaking

Preparation and Characterization of Sugarcane Bagasse Hemicellulosic Derivatives Containing Quaternary Ammonium Groups in Various Media

Homogenous Carboxymethylation of Cellulose in the Naoh/Urea Aqueous Solution