Effect of melt superheating treatment on corrosion resistance of Al2CoCrCuFeNi high entropy alloy in 0.5 M HNO3 solution
Jing Guo,Xiangfeng Xing,Xiaorong Zhang,Lingfeng Xu,Xiao Cui,Yuepeng Song,Yuan Xu
DOI: https://doi.org/10.1016/j.jallcom.2021.163284
IF: 6.2
2022-04-01
Journal of Alloys and Compounds
Abstract:Al2CoCrCuFeNi high-entropy alloy (HEA) was heated by vacuum arc furnace at different powers (5.26kW, 6.15 kW, 7.28 kW, 8.26 kW) to different temperatures above the liquidus point (labeled as T 1 , T 2 , T 3 and T 4 ). The structure and corrosion resistance were investigated by means of X-ray diffraction, scanning electron microscopy with spectroscopy (SEM/EDS), transmission electron microscopy (TEM), and electrochemical workstation. It was found that the HEAs with different superheating temperatures were all simple face-centered cubic (FCC) and body-centered cubic (BCC) solid solutions without complex phases. As the superheating temperature increased, the structure of HEAs became dense, the segregation decreased, and some fine-scale precipitations were formed at T 4 . When the heating temperature reached T 3 or higher, the corrosion current density of the alloy decreased by more than 1/2, and the range of the passivation zone also became wider, indicating that the corrosion resistance was significantly improved. It was found that the pitting potential E b ranked: T 1 <T 2 <T 4 <T 3 , indicating that the alloys labeled as T 3 and T 4 had better pitting resistance than those labeled as T 1 and T 2 . The potential range of the stable passivation region △E ranked: T 1 <T 2 <T 3 <T 4 , which proved that the passivation film on the surface of HEA became more and more stable as the superheating temperature increased.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering