Study on the properties of graphene oxide cementitious grout materials and its cementing effect in reinforcing broken rock mass by grouting
Cheng Liao,Benhai Lin,Miao Li,Songtao Hu,Guoqiang Dai,Da Liu,Shiyuan Huang
DOI: https://doi.org/10.1016/j.jobe.2024.110458
IF: 7.144
2024-08-22
Journal of Building Engineering
Abstract:The performance of grouting materials directly affects the reinforcement effect of fractured rock masses by grouting. This paper investigates the synergistic effect of graphene oxide and fly ash on the properties of cementitious grout materials and the cementing effect of grouting reinforcement on broken rock masses. Basic performance tests such as flowability, bleeding rate, and setting time of grout slurries were conducted, and macroscopic characterization were tested for flexural strength, compressive strength, permeability and resistivity of the hardened grout paste. Direct shear tests of slurry-rock interfaces were performed using a self-made shear box, and the microstructures and mineral compositions of the slurry-rock interfaces were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The test results show that the flowability, bleeding rate, and initial setting time of graphene oxide and fly ash (GO-FA) cement-based grout slurries with a water-cement ratio of 0.8 are 413 mm, 4.8 %, and 12.7 h, respectively, indicating high flowability and stability. The 28-day flexural strength, compressive strength, and permeability of GO-FA the hardened grout paste are 4.6 MPa, 25.7 MPa, and 1.50 × 10 −9 cm/s, respectively, which are 28.5 %, 30.4 %, and 25.4 % higher than those of pure cement hardened grout paste. The electrical resistivity of the hardened grout pastes increases with the curing time of the slurry and eventually stabilizes, and a linear relationship between compressive strength and electrical resistivity is established. The reinforcement effect of GO-FA grout filling on broken rock masses is the best, with significantly increased peak shear strength and residual strength of the slurry-rock interface after grouting compared to traditional cement grout filling, indicating enhanced deformation resistance and a 19.8 % increase in cohesion. Grouting filling significantly improves the cohesion and internal friction angle of fractured rock mass interfaces, with the cohesion and internal friction angle of the slurry-rock interface after grouting filling with a thickness of 1 mm being 3.90 times and 1.28 times higher, respectively, than those of the unfilled fractured surface. The filling thickness has a significant effect on cohesion but little effect on the internal friction angle. The microstructure model of the slurry-rock interface is consistent with the Xie model, indicating the generation of hydration products such as calcium hydroxide and ettringite on the interface, as well as small amounts of potassium feldspar, kaolinite, and the new mineral component calcite.
construction & building technology,engineering, civil