Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation, Modification and Property Characterization of Nano-TiO2

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

INFLUENCE OF WATER CONTENT ON CONTENT AND CHARACTERISTIC OF TiO2 DURING PREPARATION OF TiO2 NANOPARTICLES ON SiO2 SURFACE

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

pH control on preparation of nano-TiO_2 by gel-sol process

Study on modification of nano-TiO_2 coated on surface of purified diatomite

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Preparation and characterization of titanium oxide nanotubes

Study on synthesis and modification of Ti/Ce composite oxide

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Preparation and Characterization of Silica-modified Titanium Dioxide Nanoparticles by Co-precipitation Method

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Study on the Surface-Modification of Tio2 Nanoparticles

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Preparation and Characterization of Cu2+ Doped Titanium Dioxide Mesoporous Materials

Preparation and Characterization of Nano-Tio2 Powder

Preparation and Characterization of Titanium Dioxide Nanoparticle/polystyrene Composites Via Radical Polymerization

Surface Organic Modification of SiO2 ＆ Al2O3 Coated TiO2 Particles with Titanate Coupling Reagent