Abstract:In order to analyze and predict the corrosion ratio and rust layer distribution of steel rebar embedded in reinforced concrete under time-varying climatic conditions, a self-balancing steel corrosion model was established by connecting the environmental temperature, humidity, external chloride ions and oxygen concentration to the potential distribution and current density of the steel using finite element method. The model covered the whole corrosion process of steel rebar in concrete under natural climate, including the steel rebar depassivation, steel corrosion propagation and the rust layer expansion on the surface of steel rebar. In the proposed model, the microcell and macrocell corrosion were coupled by electrochemical polarization, and the cathode-to-anode area ratio was determined by the time-varying chloride distribution at the rebar surface. Taking the diffusion of chloride ions and oxygen in concrete into account, the distribution of corrosion potential of reinforcement, the change of corrosion current density of reinforcement, and the distribution of rust layer on the surface of reinforcement can be obtained based on the variation of natural temperature and humidity. The proposed model was validated utilizing the experimental data from the literatures. On this basis, a discussion about the influence of long-term climatic environments on the corrosion kinetics were conducted. The results suggest that environmental temperature and relative humidity affect the steel corrosion process mainly by affactting the chloride and oxygen diffusion coefficients, concrete resistivity, and concentration of dissolved oxygen in concrete pore solution. The corrosion current density of steel in concrete is sensitively influenced by the environmental temperature more than relative humidity. Although the initial exposure time has a significant impact on the accumulation process of chloride on steel surface within one climatic cycle, it has little influence on the final chloride distribution at the end of the period. However, the initial exposure time remarkably influences the evolution profile of rust layer thickness during the climatic cycle. The steel rebar initially exposed to a higher temperature suffers from more severe corrosion than that initially exposed to a lower temperature.

Time-dependent non-uniform corrosion of concrete structures under marine environments considering the vertical variation of exposure conditions

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

The Impact of Oxygen Availability on Steel Corrosion Considering the Self-Balance Between Anodic and Cathodic Corrosion Cells

Numerical simulation of electrochemical mechanism of steel rebar corrosion in concrete under natural climate with time-varying temperature and humidity

A Self-Balanced Electrochemical Model for Corrosion of Reinforcing Steel Bar in Considering the Micro-Environments in Concrete

Numerical Simulation of Steel Corrosion in Chloride Contaminated Concrete

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

The Vertical Non-uniform Corrosion of Reinforced Concrete Exposed to the Marine Environments

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Dynamic Electrochemical Model of Steel Corrosion in Concrete Microenvironment under Multifield Action of Heat-Moisture-Chlorine

Time-dependent reliability analysis of reinforced concrete beams subjected to bending and marine atmospheric environment

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

SIMULATED RESEARCH ON CORROSION OF REINFORCEMENT IN CONCRETE UNDER CHLORIDE ENVIRONMENT

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Atmospheric chloride-induced corrosion of steel-reinforced concrete beam exposed to real marine-environment for 7 years

Corrosion Prediction Models for Steel Bars in Chloride-Contaminated Concrete: a Review

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Statistic Investigation on Chloride Ions Distribution Based on Numerical Reconstruction of in Situ Meso-Structure of Concrete

Stochastic Characteristics of Reinforcement Corrosion in Concrete Beams under Sustained Loads