Abstract:This research program focuses on investigating the shear resistance, bond characteristics, and corrosion performance of self-consolidating concrete (SCC) compared to those of normal concrete (NC). The shear strength, cracking behavior, and deflection characteristics were tested in full-scale beams. A total of twenty reinforced concrete beams, with no shear reinforcements, were tested under mid-span concentrated load until shear failure occurred. The experimental test parameters included concrete type/coarse aggregate content, beam depth and the longitudinal reinforcing steel ratio (ρw). The beam depth ranged from 150 to 750 mm while the shear span-to-depth ratio (a/d) was kept constant in all beams, The two longitudinal reinforcing steel ratios used were 1% and 2%. The performance of SCC/NC beams was evaluated based on the results of crack pattern, crack widths, loads at the first flexure/diagonal cracking, ultimate shear resistance, post-cracking shear resistance/ductility, load-deflection response, and failure modes. Code-based equations or procedures are used to predict the crack width, first flexural cracking moment/load, and ultimate shear resistance as well as to simulate load-deflection response. The bond strength of reinforcing bars embedded in full-scale heavy reinforcing beams (4000 mm length x 1200 mm depth x 300 mm width) made with SCC was investigated and compared with that of NC. The flowability of SCC mixture through the dense reinforcement was visually monitored from a transparent formwork. The bond stress was tested for bars located at three different heights (150 mm, 510 mm, and 870 mm from the bottom of the beam) and at different concrete ages (1, 3, 7, 14 and 28 days). The bond stress-free end slip relationship, the top bar effect, and the effect of age on bond stress were investigated in both SCC and NC beams. Bond stresses predicted based on some major Codes were compared with those obtained from experiments. The corrosion of steel reinforcement embedded in full-scale SCC beams was investigated and compared to that embedded in NC beams. The corrosion performance of 400 mm width x 363 mm depth x 2340 mm length beams containing epoxy and non-epoxy coated stirrups was monitored by partial immersion in a sodium chloride solution and an impressed current. Half-cell potential tests were implemented at 25 different locations on each beam to evaluate the probability of steel corrosion along the beam length/perimeter. At the same locations where the half-cell potential tests were implemented, the chloride ion content near the bar surface was measured to study the variation of the chloride-ion penetrability along the beam length/perimeter. The mass loss and bar diameter degradation along the length of each bar were investigated at the end of the test. Predicted rebar mass loss due to corrosion based on Faraday’s law was compared with experimental mass loss for each beam.

Evolution of strength and failure of SCC during early hydration

Flexural-Shear Behavior of High-Strength Concrete Short Columns

Dynamic Evolution of Concrete Strength Grades: Insights Across Different Ages and Strain Rates

Early-Age Evolution of Strength, Stiffness, and Non-Aging Creep of Concretes: Experimental Characterization and Correlation Analysis

Experimental Study and Failure Criterion Analysis on Combined Compression-Shear Performance of Self-Compacting Concrete

Shear Strength of Strain-Hardening Cementitious Materials

Experimental study on fracture properties of self-compacting concrete

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Performance of full scale self consolidating concrete structural elements in shear, bond and under corrosion attack

Age-dependent Size Effect and Fracture Characteristics of Ultra High Performance Concrete

Study Of Flexural Response In Strain Hardening Cementitious Composites Based On Proposed Parametric Model

Cyclic Behaviour of Self-Consolidating Concrete (SCC) Filled HSS Columns

Experimental Study of Dynamic Tensile Strength of Steel-Fiber-Reinforced Self-Compacting Concrete Using Modified Hopkinson Bar

An Experimental Study of Dynamic Compression Performance of Self-Compacting Concrete

Experimental Behaviour of Self-Consolidating Concrete (SCC) Filled Hollow Structural Steel (HSS) Columns Subjected to Cyclic Loadings

Forecasting residual mechanical properties of hybrid fibre-reinforced self-compacting concrete (HFR-SCC) exposed to elevated temperatures

High-Strength Concrete in Uniaxial Tension

In-situ strength testing of high strength concrete

Inhomogeneous mechanical behaviour of concrete subjected to monotonic and cyclic loading

Experimental Investigation on Shear Behavior of the Interface between Early-Strength Self-Compacting Shrinkage-Compensating High-Performance Concrete and Ordinary Concrete Substrate

Decoupling of Autogenous Shrinkage and Tensile Creep Strain in High Strength Concrete at Early Ages