Abstract:The cyclic tensile behavior of steel-reinforced high strain-hardening ultrahigh-performance concrete (HSHUHPC) was investigated in this paper. In the experimental program, 12 HSHUHPC specimens concentrically placed in a single steel reinforcement under cyclic uniaxial tension were tested, accompanied by acoustic emission (AE) source locating technology, and 4 identical specimens under monotonic uniaxial tension were tested as references. The experimental variables mainly include the loading pattern, the diameter of the embedded steel rebar, and the level of target strain at each cycle. The tensile responses of the steel-reinforced HSHUHPC specimens were evaluated using multiple performance measures, including the failure pattern, load–strain response, residual strain, stiffness degradation, and the tension-stiffening behavior. The test results showed that the enhanced bond strength due to the inclusion of steel fibers transformed the failure pattern of the steel-reinforced HSHUHPC into a single, localized macro-crack in conjunction with a sprinkling of narrow and closely spaced micro-cracks, which intensified the strain concentration in the embedded steel rebar. Besides, it was observed that the larger the diameter of the embedded steel rebar, the smaller the maximum accumulative tensile strain under cyclic tension, which indicated that the larger the diameter of the embedded steel rebar, the greater the contribution to the tensile stiffness of steel-reinforced HSHUHPC specimens in the elastic–plastic stage. In addition, it was found that a larger embedded steel rebar appeared to reduce the tension-stiffening effect (peak tensile strength) of the HSHUHPC. Moreover, the residual strain and the stiffness of the steel-reinforced HSHUHPC were reduced by increasing the number of cycles and finally tended toward stability. Nevertheless, different target strain rates in each cycle resulted in different eventual cumulative tensile strain rates; hence the rules about failure pattern, residual strain, and loading stiffness were divergent. Finally, the relationship between the accumulative tensile strain and the loading stiffness degradation ratio under cyclic tension was proposed and the tension-stiffening effect was analyzed.

High-Strength Concrete in Uniaxial Tension

Flexural-Shear Behavior of High-Strength Concrete Short Columns

High-Strength Concrete Subjected to Triaxial Compression

Brittle behavior of high strength concrete

Durability and Compression Properties of High-Strength Concrete Reinforced with Steel Fibre and Multi-walled Carbon Nanotube

Study Of Flexural Response In Strain Hardening Cementitious Composites Based On Proposed Parametric Model

Behaviour of Large Concrete Specimens in Uniaxial Tension

Triaxial strength and failure criterion of ultra-high performance concrete

Uniaxial Tensile Experiments of Ultra-High Toughness Cementitious Composite

Uniaxial Compressive Properties of Ultra High Toughness Cementitious Composite

Empirical Relationships for Prediction of Mechanical Properties of High-Strength Concrete

Cyclic Behavior of Reinforced High Strain-Hardening UHPC under Axial Tension

Mechanical properties of high-performance concrete under triaxial compression

Experimental Study of Dynamic Tensile Strength of Steel-Fiber-Reinforced Self-Compacting Concrete Using Modified Hopkinson Bar

Damage Constitutive for High Strength Concrete in Triaxial Cyclic Compression

Compressive behaviour of circular CFDST short columns with high- and ultrahigh-strength concrete

Experimental measurement and analysis of the axial compressive stress-strain curve of Ultra High Toughness Cementitious Composites

Experimental Study On Flexural Fatigue Property Of Ultra-High Toughness Cementitious Composites

Mechanical Behaviour of Air-Entrained Concrete

A strain-hardening cementitious composites with the tensile capacity up to 8%

Flexural Behaviour of UHTCC‐layered Concrete Composite Beam Subjected to Static and Fatigue Loads