Trends in Longer-Term Corrosion Loss of Magnesium Alloys

Robert E. Melchers

DOI: https://doi.org/10.3390/cryst14020172

IF: 2.7

2024-02-09

Crystals

Abstract:The corrosion of magnesium alloys is often considered to differ in behaviour and development with time from most other metals and alloys because they show evolution of hydrogen right from first exposure. However, data extracted from the open literature indicate that magnesium alloys develop corrosion mass-loss trends with time that are consistent with the so-called bimodal pattern, which is topologically similar to those of other alloys. Examples are given of such trending for magnesium alloys under immersion, half-tide and various atmospheric exposure conditions. The critical roles of corrosion pitting and its development into localised corrosion are discussed. For high-purity magnesium alloys, the transition to longer-term corrosion, which is rate-controlled by the hydrogen evolution cathodic reaction, occurs quickly, within days. Comments are made about the application of measurements of hydrogen evolution and of electrochemical methods to make rapid estimates of shorter-term corrosion rates.

materials science, multidisciplinary,crystallography

What problem does this paper attempt to address?

The paper primarily explores the mass loss trends of magnesium alloys during long-term corrosion processes and attempts to verify whether these trends conform to the so-called "bimodal" model. By analyzing long-term corrosion data of magnesium alloys in different environments (such as seawater, atmosphere, etc.) from publicly available literature, the authors found that the trend of mass loss due to corrosion over time for magnesium alloys shows similarities to the "bimodal" pattern exhibited by most other metals and their alloys.

Specifically, the paper first introduces the importance of magnesium alloys in practical applications due to their lightweight characteristics, as well as their issues, such as relatively low strength and corrosion resistance. Subsequently, the paper focuses on the unique aspects of the corrosion behavior of magnesium alloys—namely, the observation of hydrogen gas generation from the initial exposure, a phenomenon known as the "negative difference effect" or "anomalous hydrogen evolution."

The core part of the paper analyzes the mass loss data of magnesium alloys under different environmental conditions over various time spans (up to 16 years). These data come from various experimental projects, including early long-term field tests conducted by the U.S. Navy in the Panama Canal area and more recent tests conducted in China and other locations. Through the analysis of these data, the authors point out that the trend of mass loss due to corrosion over time for magnesium alloys is neither linear nor fully consistent with the traditional power law function but shows significant nonlinear characteristics, especially in the initial years. These trends are consistent with the predictions of the "bimodal" model.

Finally, the paper discusses the critical role of pitting and localized corrosion in the corrosion process of magnesium alloys and how these phenomena affect the rate of hydrogen evolution and the results of electrochemical measurements. Overall, the paper aims to confirm the time trends of mass loss due to corrosion of magnesium alloys through empirical research and to explore the mechanisms behind these trends.