Abstract:To explore efficient non-noble metal-based electrocatalysts for oxygen reduction reaction (ORR), herein we developed a facile bottom-up approach for the fabrication of a hollow porous carbon sphere codoped with ultrasmall Co nanoparticles and uniform nitrogen distribution (Co-HNCS) via one-step pyrolysis of a core-shell type precursor composing of polystyrene (PS) core and bimetallic ZIF (zeolite imidazolate framework) shell. The bimetallic Co-Zn-ZIFs (BMZIFs) was selected as the sacrifice template due to not only its high nitrogen content and regular porosity but also the superiority that Zn species in BMZIFs can both spatially separate Co species to suppress the aggregation of ultra-small Co NPs and be evaporated to afford extra pores during high-temperature pyrolysis. As expected, by adjusting the starting molar ratio of Zn to Co, we were able to prepare Co-HNCS-x (x represent the molar ratio of Co to total starting metal feeding) that exhibited unique hollow structure with large surface areas, enhanced mass transport, high porosities, tunable particle sizes and graphitization degrees, abundant highly active CoNx sites, and thus significantly improved ORR performance. Particularly, the optimal Co-HNCS-0.2 exhibited the remarkable ORR activity (the onset and half-wave potentials were 0.94 and 0.82 V vs. RHE, respectively) via an efficient four-electron-dominant ORR process in alkaline medium, which outperformed that of commercial Pt/C (20 wt%, the onset and half-wave potentials were 0.93 and 0.80 V vs. RHE, respectively) and most of previously reported Co-based catalysts. Moreover, it also displayed much superior stability and tolerance to methanol as compared to Pt/C, further highlighting the merit of this facile synthesis approach. Our findings might inspire new thoughts on the development of precious-metal-free, highly-efficient and cost-effective ORR electrocatalysts derived from MOF.

Inner-pore reduction nucleation of palladium nanoparticles in highly conductive wurster-type covalent organic frameworks for efficient oxygen reduction electrocatalysis

Synergistic Modulating Interlayer Space and Electron-Transfer of Covalent Organic Frameworks for Oxygen Reduction Reaction

A 3D Covalent Organic Framework with In-situ Formed Pd Nanoparticles for Efficient Electrochemical Oxygen Reduction

Conjugated Covalent Organic Frameworks as Platinum Nanoparticle Supports for Catalyzing the Oxygen Reduction Reaction

Modulating the Oxygen Reduction Reaction Performance via Precisely Tuned Reactive Sites in Porphyrin-Based Covalent Organic Frameworks

Hollow Porous Carbon-Confined Atomically Ordered PtCo3 Intermetallics for an Efficient Oxygen Reduction Reaction

Co Nanoparticles Confined in Mesoporous Mo/N Co-Doped Polyhedral Carbon Frameworks Towards High-Efficiency Oxygen Reduction

Bimetal Metal‐Organic Frameworks Derived Hierarchical Porous Cobalt@Nitrogen‐Doped Carbon Tubes As an Efficient Electrocatalyst for Oxygen Reduction Reaction

Fully‐Conjugated Covalent Organic Frameworks with Two Metal Sites for Oxygen Electrocatalysis and Zn–Air Battery

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

Achieving efficient oxygen reduction on ultra-low metal-loaded electrocatalysts by constructing well-dispersed bimetallic sites and interconnected porous channels

Metal-Organic-Framework-Derived Co2 P Nanoparticle/Multi-Doped Porous Carbon As a Trifunctional Electrocatalyst.

Conductive bimetal organic framework nanorods decorated with highly dispersed Co 3 O 4 nanoparticles as bi-functional electrocatalyst

Crystalline/Amorphous Co2P@FePO4 Core/Shell Nanoheterostructures Supported on Porous Carbon Microspheres as Efficient Oxygen Reduction Electrocatalysts

Highly Efficient Co―N―C Electrocatalysts with a Porous Structure for the Oxygen Reduction Reaction

Metal-organic Framework Assembly Derived Hierarchically Ordered Porous Carbon for Oxygen Reduction in Both Alkaline and Acidic Media

Metal–Organic Framework‐Derived Co 2 P Nanoparticle/Multi‐Doped Porous Carbon as a Trifunctional Electrocatalyst

In-situ Coupling FeN Nanocrystals with Fe/Fe3C Nanoparticles to N-doped Carbon Nanosheets for Efficient Oxygen Electrocatalysis

Rational Design of Hollow N/Co-doped Carbon Spheres from Bimetal-Zifs for High-Efficiency Electrocatalysis

Exploring Efficient Fe/N/C Electrocatalysts for Oxygen Reduction from Nonporous Interpenetrated Metal–Organic Framework Involving in Situ Formation of ZnO Templates

Bimetal–Organic Framework Self-Adjusted Synthesis of Support-Free Nonprecious Electrocatalysts for Efficient Oxygen Reduction