Carboxyl induced ultrahigh defects and boron/nitrogen active centers in cobalt-embedded hierarchically porous carbon nanofibers: The stable oxygen reduction reaction catalysis in acid
Mian Li,Fei Guo,Lan Xiao,Yibin Wang,Yingjie Zhang,Xiangjie Bo,Tingting Liu
DOI: https://doi.org/10.1016/j.jcis.2023.01.065
IF: 9.9
2023-01-22
Journal of Colloid and Interface Science
Abstract:Transition metal-nitrogen-carbon (M–N–C) type catalysts have been considered a promising alternative to noble metals for oxygen reduction reaction (ORR) electrocatalysis. Nevertheless, poor stabilities of M–N–C catalysts in acidic solutions limit their commercialization. In this study, we design and synthesize novel three-dimensional (3D) cobalt (Co) nanoparticles encapsulated in ultrahigh content of boron (B) and nitrogen (N) -doped hierarchically porous carbon nanofibers (denoted as ) by carbonizing the 3D acetic acid/cobalt nitrate/4-hydroxybenzeneboronic acid/polyvinylpyrrolidone precursor networks woven using electrospinning method under a nitrogen atmosphere. The optimal catalyst has abundant micro/mesopores and numerous topological defects and exhibits the largest surface area. Under the synergistic effect of oxygen-containing acetic acid molecules and the electrospinning technology, 5.87 at.% of B and 5.91 at.% of N atoms were doped into carbon nanofibers. Specifically, B/N electrocatalytic active centers (including BC 3 , pyridinic-N/Co–N–C, pyrrolic-N, and graphitic-N) of approximately 8.70 at.% were successfully introduced into the skeletons of In 0.1 M KOH, the ORR onset potential ( E onset ) and half-wave potential ( E 1/2 ) of were ∼64 and ∼63 mV, respectively, more positive than those of 20 wt .% Pt/C. Additionally, in 0.5 M H 2 SO 4 , the ORR E onset and E 1/2 values of were only ∼11 and ∼7 mV, respectively, more negative than those of 20 wt. % Pt/C. As the 3D hierarchically porous architectures, topological carbon edges, BC 3 , and partial N-C/Co–N–C are relatively stable, the exhibits excellent stability toward ORR catalysis in both acidic and basic media. These favorable properties of nanofibers make them the best non-noble metal-based carbonaceous electrocatalysts for ORR in acidic electrolytes.
chemistry, physical