Abstract:Development of nonprecious metal catalysts for oxygen reduction reaction (ORR) to reduce or eliminate Pt-based electrocatalysts is of great importance for fuel cells. Herein, Co/N-codoped carbon with carbon nanofiber (CNF) interconnected three-dimensional (3D) frameworks and graphitic carbon-encapsulated Co nanoparticles were designed and successfully prepared via the in situ growth of zeolitic imidazolate framework-67 (ZIF67) with biomass nano-microfibrillar cellulose (MFC) and then pyrolysis. The catalyst (Co/) exhibited outstanding long-term catalytic durability with 92.7% current retention after 70 000 s, which was much higher than that of commercial Pt/C in alkaline media. The support and connection of CNFs to Co/N-C frameworks and the protection of Co nanoparticles by graphite layers contribute to their impressive long-term catalytic stability. Meanwhile, Co/ displayed excellent ORR catalytic performance (E0 = 0.952 V vs RHE, E1/2 = 0.852 V vs RHE, and n: 4.2) in alkaline media. This strategy provides new insights into developing advanced nonprecious metal carbon-based catalysts for ORR.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12069?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12069</a>.High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and the corresponding element distribution maps (a,b) of Co/N-C; Raman spectra of Co/N-C, Co/, and CNFs; N2 adsorption/desorption isotherms and H–K pore size distributions (inset: BJH pore size distributions) of ZIF67 and ; LSV curves and K–L plots of Co/N-C (a,b) in 0.1 M KOH at 10 mV s–1; I–t chronoamperometric response of Co/N-C, Co/, and Pt/C 20% with 1600 rpm rotation speed in 0.5 M H2SO4 for 10 000 s (a) and I–t chronoamperometric response of Co/N-C and Co/ with a rotation speed of 1600 rpm in O2-bubbled 0.5 M H2SO4 for 70 000 s (b); elemental composition of the as-prepared samples tested by XPS and Co content determined by ICP (Table S1); comparison of ORR activity and stability between Co/ and other reported electrocatalysts (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12069/suppl_file/am0c12069_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

What problem does this paper attempt to address?

### Problems the Paper Aims to Solve The paper aims to develop an efficient and stable non-precious metal catalyst for the oxygen reduction reaction (ORR) to reduce or replace the commonly used platinum-based electrocatalysts in fuel cells. Specifically, the researchers designed and successfully prepared a three-dimensional (3D) framework material based on cobalt and nitrogen co-doped carbon (Co/N-C), which consists of interconnected carbon nanofibers (CNFs) and cobalt nanoparticles (Co nanoparticles) wrapped in a graphite carbon layer. This catalyst exhibits excellent long-term catalytic stability and efficient ORR catalytic performance in alkaline media. ### Main Issues and Solutions 1. **Limitations of Platinum-based Catalysts**: - Platinum-based catalysts are expensive, have limited reserves, and face various stability issues, restricting their large-scale commercial application. - The researchers proposed a non-precious metal catalyst based on cobalt and nitrogen co-doped carbon (Co/N-C) to replace platinum-based catalysts. 2. **Long-term Stability of Catalysts**: - Non-precious metal catalysts (such as M/N-C) tend to undergo metal dissolution and carbon oxidation during long-term use, leading to a decline in catalytic activity. - By increasing the degree of graphitization and protecting metal nanoparticles with a graphite carbon layer, the long-term stability of the catalyst can be effectively improved. 3. **Preparation Method of the Catalyst**: - Using nanofibrillated cellulose (MFC) as a template, Co/N-C@CNFs with an interconnected 3D framework structure were prepared by in-situ growth of zeolitic imidazolate framework-67 (ZIF67) followed by pyrolysis. - This method not only improves the dispersion and graphitization degree of the catalyst but also enhances its long-term stability. ### Experimental Results - **Morphology and Structural Characterization**: - SEM and TEM images show that Co/N-C@CNFs have a clear polyhedral framework structure, with Co nanoparticles uniformly dispersed and completely wrapped by a graphite carbon layer. - Compared to Co/N-C without CNFs, Co/N-C@CNFs exhibit a higher degree of graphitization and a smoother surface. - **Electrocatalytic Performance**: - In alkaline media, Co/N-C@CNFs have a higher onset potential (E0=0.952 V vs. RHE) and half-wave potential (E1/2=0.852 V vs. RHE) than commercial Pt/C catalysts. - In acidic media, Co/N-C@CNFs also show good ORR catalytic performance, although slightly lower than in alkaline media. ### Conclusion By introducing carbon nanofibers (CNFs) and a graphite carbon layer, the researchers successfully prepared an efficient and stable Co/N-C@CNFs catalyst, which exhibits excellent ORR catalytic performance and long-term stability in alkaline media. This strategy provides new insights for the development of advanced non-precious metal carbon-based catalysts.

ZIF67@MFC-Derived Co/N-C@CNFs Interconnected Frameworks with Graphitic Carbon-Encapsulated Co Nanoparticles as Highly Stable and Efficient Electrocatalysts for Oxygen Reduction Reactions

Noble-metal-free Co-N-c Catalyst Derived from Cellulose-Based Poly(ionic Liquid)s for Highly Efficient Oxygen Reduction Reaction.

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

ZIF-8/ZIF-67-Derived Co-N-x-Embedded 1D Porous Carbon Nanofibers with Graphitic Carbon-Encased Co Nanoparticles As an Efficient Bifunctional Electrocatalyst

ZIF67-ZIF8@MFC-Derived Co-Zn/NC Interconnected Frameworks Combined with Perfluorosulfonic Acid Polymer as a Highly Efficient and Stable Composite Electrocatalyst for Oxygen Reduction Reactions

N-doped Carbon-Stabilized PtCo Nanoparticles Derived from Pt@ZIF-67： Highly Active and Durable Catalysts for Oxygen Reduction Reaction

A “MOFs plus ZIFs” Strategy toward Ultrafine Co Nanodots Confined into Superficial N-Doped Carbon Nanowires for Efficient Oxygen Reduction

Core-Shell ZIF-67@ZIF-8-derived multi-dimensional cobalt-nitrogen doped hierarchical carbon nanomaterial for efficient oxygen reduction reaction

Co nanoparticle embedded in atomically-dispersed Co-N-C nanofibers for oxygen reduction with high activity and remarkable durability

Cobalt@Nitrogen‐Doped Porous Carbon Fiber Derived from the Electrospun Fiber of Bimetal–Organic Framework for Highly Active Oxygen Reduction

In Situ Anchoring of Zeolite Imidazole Framework-Derived Co, N-Doped Porous Carbon on Multiwalled Carbon Nanotubes Toward Efficient Electrocatalytic Oxygen Reduction

Co nanoparticles embedded N-doped hierarchical porous carbon matrix as an efficient electrocatalyst for oxygen reduction reaction

Facile synthesis of three-dimensional Co/N co-doped carbon nanocuboid for enhanced oxygen reduction reaction

A carbon catalyst doped with Co and N derived from the metal-organic framework hybrid (ZIF-8@ZIF-67) for efficient oxygen reduction reaction

Hierarchical N-doped carbon spheres anchored with cobalt nanocrystals and single atoms for oxygen reduction reaction

Cobalt-Copper-Embedded Nitrogen-Doped Carbon Nanostructures Derived from Zeolite Imidazolate Frameworks as Electrocatalysts for the Oxygen Reduction Reaction

Ultralong nitrogen/sulfur Co‐doped carbon nano‐hollow‐sphere chains with encapsulated cobalt nanoparticles for highly efficient oxygen electrocatalysis

Enhancing Defects of N-Doped Carbon Nanospheres Via Ultralow Co Atom Loading Engineering for a High-Efficiency Oxygen Reduction Reaction

A high-performance nitrogen-rich ZIF-8-derived Fe-Co-NC electrocatalyst for the oxygen reduction reaction

Three-dimensional porous g-C 3 N 4 nanosheet, CNT and ZIF-8@ZIF-67-derived carbon nanoarchitecture composite as oxygen reduction electrocatalyst

Mn/Co co-doped porous carbon material derived from self-assembly of CoPc and ZIF-11 for oxygen reduction reaction