Abstract:In this study, carbon blocks were fabricated using isotropic coke and coal tar pitch as raw materials, with a variation in pressure during cold isostatic pressing (CIP). The CIP pressure was set to 50, 100, 150, and 200 MPa, and the effect of the CIP pressure on the mechanical and electrical properties of the resulting carbon blocks was analyzed. Microstructural observations confirmed that, after the kneading, the surface of isotropic coke was covered with the pitch components. Subsequently, after the CIP, granules, which were larger than isotropic coke and the kneaded particles, were observed. The formation of these granules was attributed to the coalescence of kneaded particles under the applied pressing pressure. This granule formation was accompanied by the development of pores, some remaining within the granules, while others were extruded, thereby existing externally. The increase in the applied pressing pressure facilitated the formation of granules, and this microstructural development contributed to enhanced mechanical and electrical properties. At a pressing pressure of 100 MPa, the maximum flexural strength was achieved at 33.3 MPa, and the minimum electrical resistivity was reached at 60.1 μΩm. The higher the pressing pressure, the larger the size of the granules. Pores around the granules tended to connect and grow larger, forming crack-like structures. This microstructural change led to degraded mechanical and electrical properties. The isotropic ratio of the carbon blocks obtained in this study was estimated based on the coefficient of thermal expansion (CTE). The results confirmed that all carbon blocks obtained proved to be isotropic. In this study, a specimen type named CIP-100 exhibited the best performance in every aspect as an isotropic carbon block.

Effect of soft-mould pressing method on anisotropy of the graphitic matrix spheres: Dry-bag isostatic vs. Quasi-isostatic

Research on Manufacture Technology of Spherical Fuel Elements by Dry-Bag Isostatic Pressing

The Effect of Stress Levels on the Coefficient of Thermal Expansion of a Fine-Grained Isotropic Nuclear Graphite

The electrochemical deconsolidation mechanism of graphite matrix in HTGR spherical fuel elements

Studies on the dimensional and mass changes of spherical fuel element during the heat treatment

Advantages of Natural Microcrystalline Graphite Filler over Petroleum Coke in Isotropic Graphite Preparation

Response surface optimization and finite element simulation to prepare microporous carbon refractories via cold isostatic pressing

Study on Preparation of Isotropic Graphite With Natural Amorphous Graphite

Pulverization and Spheroidization of Natural Graphite Powder for the Matrix Graphite in High-Temperature Gas-Cooled Reactors

The Influence of Pores on Irradiation Property of Selected Nuclear Graphites

Study on the Effective Diffusion Coefficient of Inert Gases in Porous Graphite Materials

Fabrication of Spherical Fuel Element for 10 MW High Temperature Gas-cooled Reactor

Optimization of Preparation Process and Study on the Properties and Microstructures of Nuclear Natural Graphite Powder for HTR Pebble Fuel Elements

Effect of Microstructural Change under Pressure during Isostatic Pressing on Mechanical and Electrical Properties of Isotropic Carbon Blocks

SiC/SiO2 Coating on Matrix Graphite Spheres of HTR Fuel Element Produced by a Two-Step Pack Cementation/High-Temperature Oxidation Process

Fabrication of Matrix Graphite with a High Degree of Graphitization for Spherical Fuel Elements by Using Natural Microcrystalline Graphite Fillers

Hot-pressing of BeO Ceramics and Its Thermal Conductivity and Flexural Strength

Densification of matrix graphite for spherical fuel elements used in molten salt reactor via addition of green pitch coke

Effect of water molecules co-intercalation and hydrolysis on the electrochemical deconsolidation of matrix graphite in aqueous nitric acid

Anisotropy of Coefficient of Thermal Expansion of Nuclear Graphite under Compressive Stresses

Effect of pore structure on the thermophysical and frictional properties of high-density graphite