Abstract:A boron-rich boron-carbide material (B4+δC) was synthesized by spark plasma sintering of a ball-milled mixture of high-purity boron powder and graphitic carbon at a pressure of 7 MPa and a temperature of 1930 °C. This high-pressure, high-temperature synthesized material was recovered and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, Vickers hardness measurements, and thermal oxidation studies. The X-ray diffraction studies revealed a single-phase rhombohedral structure (space group R-3m) with lattice parameters in hexagonal representation as a = 5.609 ± 0.007 Å and c = 12.082 ± 0.02 Å. The experimental lattice parameters result in a value of δ = 0.55, or the composition of the synthesized compound as B4.55C. The high-resolution scans of boron binding energy reveal the existence of a B-C bond at 188.5 eV. Raman spectroscopy reveals the existence of a 386 cm-1 vibrational mode representative of C-B-B linear chain formation due to excess boron in the lattice. The measured Vickers microhardness at a load of 200 gf shows a high hardness value of 33.8 ± 2.3 GPa. Thermal gravimetric studies on B4.55C were conducted at a temperature of 1300 °C in a compressed dry air environment, and its behavior is compared to other high-temperature ceramic materials such as high-entropy transition metal boride. The high neutron absorption cross section, high melting point, high mechanical strength, and thermal oxidation resistance make this material ideal for applications in extreme environments.

Hard Copper Boride with Exceptional Conductivity

Superhard solid solutions of diamond and cubic boron nitride

Superhard high-entropy dodecaboride with high electrical conductivity

Fabrication of Alkali Metal Boride: Honeycomb‐Like Structured NaB4 with High Hardness and Excellent Electrical Conductivity

Formation of copper boride on Cu(111)

Revealing the Unusual Boron-Pinned Layered Substructure in Superconducting Hard Molybdenum Semiboride

Superhard and superconductive polycrystalline boron doped diamond synthesized with different concentration of B 4 C

Synthesis and Thermal Oxidation Resistance of Boron-Rich Boron-Carbide Material

Experimental evidence of surface copper boride

Superhard and Superconducting B6C

Hardness and superconductivity in tetragonal LiB4 and NaB4

Depositing boron on Cu(111): Borophene or boride?

Is Orthorhombic Iron Tetraboride Superhard?

Boron-Rich Molybdenum Boride with Unusual Short-Range Vacancy Ordering, Anisotropic Hardness, and Superconductivity

Superhard sp<SUP>2</SUP>-sp<SUP>3</SUP> hybridized B<sub>2</sub>C<sub>3</sub>N<sub>2</sub> with 2D metallicity

Enhanced hardness and conductivity motivated by Ni and Co doping in β-MoB2

Superconducting boron allotrope featuring pentagonal bipyramid at ambient pressure

Prediction of fully metallic σ-bonded boron framework induced high superconductivity above 100 K in thermodynamically stable Sr2B5 at 40 GPa

Coexistence of Superconductivity and Superhardness in Beryllium Hexaboride Driven by Inherent Multicenter Bonding.

3D Porous Metallic Boron Carbide Crystal Structure with Excellent Ductility

On the structures and bonding of copper boride nanoclusters, Cu2B– (x = 5–7)