Abstract:External pressure can greatly affect the cycling performance of solid-state batteries, although pressure-driven changes in electrochemical processes are still not fully understood. For instance, Li10GeP2S12 (LGPS) is known to strongly react with lithium metal. However, under external pressure, with the use of additional Li6PS5Cl (LPSCl) outer layers forming a sandwich structure, stable cycling over 1800 cycles can be achieved (Ye and Li. Nature, 2021, 593, 218–222). This finding motivated us to investigate the interfacial behavior of Li/LGPS under external pressure (i.e., 7.5 MPa) to shed light on the improved electrochemical performance. Our results indicate that the growth rate of the interfacial resistance is substantially decreased while the cycle life before open-circuit failure is substantially extended under the MPa-scale external pressure. The reactivity between lithium metal and LGPS is extremely severe, forming island features upon cycling. Using selected area Raman spectroscopy, these “islands” were confirmed to be interfacial decomposition products, in line with the expected volume expansion of LGPS when reacting with lithium metal. Under 7.5 MPa external pressure, the interface products were formed in a densely packed and homogeneously distributed manner after 10 cycles. While the application of external pressure did not alter the types of interface components, the MPa-level pressure functioned in improving physical contact of the interface and homogenizing the interface reactions. In addition, a lithium depletion layer was formed in the interface region, which can contribute to extra interfacial resistance. Our work marks an important step to understanding the interfacial electrochemical behavior of the Li/LGPS interface under an MPa-scale external pressure.

Effects of external pressure on cycling performance of silicon-based lithium-ion battery: modelling and experimental validation

Effect of Mechanical Pressure on Lifetime, Expansion, and Porosity of Silicon-Dominant Anodes in Laboratory Lithium-Ion Cells

Cycling-induced damage of silicon-based lithium-ion batteries: Modeling and experimental validation

A stress-based charging protocol for silicon anode in lithium-ion battery: Theoretical and experimental studies

Interfacial Behavior of a Thio-LISICON Solid-State Electrolyte under External Pressure

Investigation into the impact of charging rates on the stress development within silicon composite electrodes

Understanding the Effect of Cycling Lithium-Ion Pouch Cells under Stress Using Neutron Diffraction

Design of Silicon-Based Porous Electrode in Lithium-Ion Batteries: Insights from Multiscale Electrode Model Simulations

Effect of external pressure and internal stress on battery performance and lifespan

Insights into the Swelling Force in Commercial LiFePO4 Prismatic Cell

The Beneficial Effect of Pressure for Lithium Ion Battery Cells through Gas Dissipation

Stress Evolution in Lithium-ion Composite Electrodes during Electrochemical Cycling and Resulting Internal Pressures on the Cell Casing

Effect of Mechanical Pressure on Rate Capability, Lifetime, and Expansion in Multilayer Pouch Cells with Silicon-Dominant Anodes

Mechanical behavior of Silicon-Graphite pouch cells under external compressive load: Implications and opportunities for battery pack design

Internal pressure regulation enables reliable electrochemical performance evaluation of lithium-ion full coin cell

In-situ obtained internal strain and pressure of the cylindrical Li-ion battery cell with silicon-graphite negative electrodes

How Does External Pressure Shape Li Dendrites in Li Metal Batteries?

External-pressure–electrochemistry Coupling in Solid-State Lithium Metal Batteries

An mechanical/thermal analytical model for prismatic lithium-ion cells with silicon‐carbon electrodes in charge/discharge cycles

Modeling of Coupling Between Free Volume Evolution and Diffusion in Silicon Electrodes of Lithium-Ion Batteries

Modelling and analysis of the volume change behaviors of Li-ion batteries with silicon-graphene composite electrodes