Abstract:ZrO 2 ceramics are commonly known as 'hard and brittle' materials due to their exceptional properties, such as high hardness, heat resistance, chemical stability, and low thermal conductivity. However, the hole processing technique for ZrO 2 ceramics often results in significant tool wear and compromises the quality of the holes. This study investigates the removal mechanism of ZrO 2 ceramic materials by using carbide tools, diamond-coated carbide tools, and micro-sintered tools. It also analyzes the impact of processing parameters on the wear mechanism of different tools and the quality of hole processing in ZrO 2 ceramics. The findings revealed that at high spindle speed (8000 r/min) and low feed rate (1 mm/min), the diamond coating on the rake surface of the diamond-coated carbide tool tends to peel off, leading to the formation of sharp edges on the flank surface. This phenomenon results in a reduction in thrust forces. Moreover, it is observed that as the number of hole machining operations increases, the peeling of the diamond coating on the tool flank becomes more severe. The increase in feed rate causes the diamond coating peeling area on the rake face of the tool to expand toward the chisel edge and even reach the thinned edge area near the chisel edge. When the feed rate of carbide tools increases, the wear degree of the chisel edge gradually increases, while the wear degree of the main cutting edge corner position gradually decreases. At low spindle speeds, the main cutting edge breaks and the cutter head is also damaged and deformed. The main wear mechanisms of micro-sintered tools involve shedding, fragmentation, wear, and adhesion of diamond abrasive grains. The bottom surface of the tool tends to accumulate a significant amount of flaky adhesion, which dulls the tool and increases thrust force. In contrast to carbide tools, diamond-coated carbide tools offer improved hole exit quality. However, micro-sintered tools often exhibit large volumes of flaking at the hole exits, resulting in shell-like stripes on the peeled surface.

Wear characteristics of zirconia-toughened epoxy/Kevlar-honeycomb composite lining for drilling casing

Tribological Characterization of a Novel Ceramic–Epoxy–Kevlar Composite

Research On Wear Behavior Of Atc Cermet Material

Wear Behavior of Special Tools in the Drilling of CFRP Composite Laminates

Tribological Behaviors of the Diamond Films Sliding Against the T800/X850 CFRP Laminates

Wear behaviour of CVD diamond-coated tools in the drilling of woven CFRP composites

Probing the Effect of Cuttings Particle Size on the Friction and Wear Mechanism at the Casing Friction Interface: A Molecular Dynamics Study

Interfacial characterization and erosive wear performance of zirconia toughened alumina ceramics particles reinforced high chromium white cast irons composites

Comparative study of tool wear mechanisms in drilling ZrO2 ceramics using various tool types

Impact-abrasive wear property of ZrO2 toughened Al2O3 ceramic particles reinforced high manganese steel matrix composites

Interfacial characteristics and wear performances of iron matrix composites reinforced with zirconia-toughened alumina ceramic particles

Effect of Impact Force on the Impact-Sliding Wear of Titanium Alloy Drill Pipes against Steel Casings

Microstructure and Wear Behavior of Graphene Nanosheets-Reinforced Zirconia Coating

Elucidation of Abrasive Wear and Slurry Erosion Behavior of Fe Matrix Composites Reinforced with Metallic Coating Modified ZTAP Ceramics

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

Tribological Performance of In-Situ Epoxy Composites Filled with Micro-Sized ZrB 2 Particles

Effects of Impact Energy, Impact Frequency, and Test Time on Impact Wear Characteristics of Zirconia-Toughened Alumina Particles-Iron (ZTAp-Fe) Composites Using Response Surface Methodology

Wear Behavior of Epoxy Resin Reinforced with Ceramic Nano- and Microparticles

The Tribological Properties of Kevlar Pulp Reinforced Epoxy Composites under Dry Sliding and Water Lubricated Condition

Tribological Performances of Diamond Film and Graphite/diamond Composite Film

A Study of Parameters Affecting Wear Resistance of Alumina and Yttria Stabilized Zirconia Composite Coatings on Al-6061 Substrate