Amorphous and homogeneously Zr-doped MnOx with enhanced acid and redox properties for catalytic oxidation of 1,2-Dichloroethane
Gong Chen,Dongsen Hong,Hangqi Xia,Wei Sun,Shijie Shao,Binwei Gong,Shun Wang,Jinyan Wu,Xingyi Wang,Qiguang Dai
DOI: https://doi.org/10.1016/j.cej.2021.131067
IF: 15.1
2022-01-01
Chemical Engineering Journal
Abstract:<p>Series of MnO<sub>x</sub> based catalysts were prepared and investigated for 1,2-dichloroethane (1,2-DCE) oxidation. R-ZrMn prepared by a novel reflux method presented an amorphous structure and homogeneous dispersion of Zr, which prominently enhanced acid and redox properties, such as more surface oxygen species and vacancies (O<sub>Ads</sub>/O<sub>Latt</sub> = 0.53), better reducibility, severer Jahn-Teller distortion, more total acid amount (396 μmol·g<sup>−1</sup>) and Brønsted acid sites. Compared with the pristine MnO<sub>x</sub> and ZrO<sub>2</sub>, R-ZrMn exhibited a better catalytic activity for 1,2-DCE oxidation (T<sub>90</sub> = 287 °C and the reaction rate at 150 °C was 5.13 μmol min<sup>−1</sup>·g<sup>−1</sup>), less formation of chlorinated by-products, high durability and resistance-H<sub>2</sub>O. Catalytic oxidation of 1,2-DCE and the formation of chlorinated by-products on MnO<sub>x</sub> based catalysts was typically represented as a synergistic catalysis process of acid and redox sites, and a positive relationship between total acid amount or O<sub>Ads</sub>/O<sub>Latt</sub> and reaction rate of 1,2-DCE oxidation was clearly observed. Meanwhile, a possible mechanism and formation pathway were proposed.</p>
engineering, chemical, environmental