Understanding the anti-corrosion characteristics of surface modification of h-BN and carbon nanotubes/magnesium composites in simulated seawater

Victor Sunday Aigbodion,Abdulmajeed Abdullah Alayyaf,Chinemerem Jerry Ozoude

DOI: https://doi.org/10.1039/d4ra04076g

2024-08-02

Abstract:In order to address the issues of wettability and scattering between matrix and reinforcement and enhance corrosion resistance, the effects of incorporating hexagonal boron nitride (h-BN) into magnesium-carbon nanotubes (Mg-0.5 wt% CNTs) nanocomposites were successfully investigated. An inventive coating with h-BN using a novel electroless chemical deposition technique and double stir casting were used. The composites were produced by varying weight percentages of h-BN (0, 2, 4, and 6). The corrosion testing, microstructural analysis, and physical testing of the samples were carried out. A corrosion resistance of 75.1% was obtained when the 4 weight percent of h-BN content was compared to Mg-0.5% wt% CNTs. Even though the relative density increased noticeably, this was due to the uniform dispersion of h-BN nanoparticles over the entire surface. Researchers have established that adding 4 wt% h-BN to the Mg-0.5 wt% CNT nanocomposite can improve the wettability between Mg and CNTs and enhance the corrosion resistance properties.