Anticorrosive performance of waterborne epoxy coatings containing water-dispersible hexagonal boron nitride (h-BN) nanosheets

Mingjun Cui,Siming Ren,Jia Chen,Shuan Liu,Guangan Zhang,Haichao Zhao,Liping Wang,Qunji Xue

DOI: https://doi.org/10.1016/j.apsusc.2016.11.141

IF: 6.7

2017-03-01

Applied Surface Science

Abstract:Homogenous dispersion of hexagonal boron nitride (h-BN) nanosheets in solvents or in the polymer matrix is crucial to initiate their many applications. Here, homogeneous dispersion of hexagonal boron nitride (h-BN) in epoxy matrix was achieved with a water-soluble carboxylated aniline trimer derivative (CAT−) as a dispersant, which was attributed to the strong π-π interaction between h-BN and CAT−, as proved by Raman and UV–vis spectra. Transmission electron microscopy (TEM) analysis confirmed a random dispersion of h-BN nanosheets in the waterborne epoxy coatings. The deterioration process of water-borne epoxy coating with and without h-BN nanosheets during the long-term immersion in 3.5wt% NaCl solution was investigated by electrochemical measurements and water absorption test. Results implied that the introduction of well dispersed h-BN nanosheets into waterborne epoxy system remarkably improved the corrosion protection performance to substrate. Moreover, 1wt% BN/EP composite coated substrate exhibited higher impedance modulus (1.3×106Ωcm2) and lower water absorption (4%) than those of pure waterborne epoxy coating coated electrode after long-term immersion in 3.5wt% NaCl solution, demonstrating its superior anticorrosive performance. This enhanced anticorrosive performance was mainly ascribed to the improved water barrier property of epoxy coating via incorporating homogeneously dispersed h-BN nanosheets.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films