Large‐Area Deep‐Blue Polymer Light‐Emitting Diodes with Well‐Resolved Emission from Planar Conformational Segments Fabricated via Brush Coating
Man Xu,Chuanxin Wei,Shengjie Wang,Jingrui Zhang,Jingyao Ma,Ning Sun,Lili Sun,Yamin Han,Lubing Bai,Jinyi Lin,Jiawei Qiao,Xiatao Hao,Wei Xue,Linghai Xie,Wei Huang
DOI: https://doi.org/10.1002/adom.202300035
IF: 9
2023-03-14
Advanced Optical Materials
Abstract:Large‐area deep‐blue polymer light‐emitting diodes (PLEDs) based on polydiarylfluorenes are manufactured via brush‐coated processing. Large‐area brush‐coated films present a uniform, well‐defined, and deep‐blue emission, attributed to the intramolecular singlet excitonic behavior from the planar conformation segment without any interchain charge‐transfer states. Large‐area, efficient, and stable brush‐coated PLEDs are achieved with a well‐resolved and narrowband emission with CIE chromaticity coordinates of (0.15, 0.10). The fabrication of large‐area printed deep‐blue polymer light‐emitting diodes (PLEDs) is a prerequisite for solid‐state lighting and flat‐panel displays. However, manufacturing large‐area narrow‐band deep‐blue PLEDs remains a challenging task owing to the difficulties in reducing structural distortions caused by the transitions from the ground to excited states. Herein, large‐area deep‐blue PLEDs with narrow‐band emission from the planar (β) conformational segments of polydiarylfluorenes are fabricated via brush coating. First, large‐area uniform brush‐coated films (4 × 4 cm2) with a relatively smooth morphology are manufactured. They produce strong, stable, and narrow‐band deep‐blue emission (full width at half maximum (FWHM): 29 nm for the 0–0 and 0–1 emission peaks), which results from single β‐conformational segments without a charge transfer state. Therefore, owing to their efficient emission and excellent printing capability, large‐area brush‐coated PLEDs with an emission area of 3 × 3 cm2 and uniform deep‐blue emission (FWHM: 27 nm; CIE chromaticity coordinate: (0.15, 0.10), brightness: 3780 cd m−2) are obtained, and their maximum external quantum efficiency (1.79%) is two times higher than those of the devices containing spin‐coated films. Finally, considering the key role of deep‐blue PLEDs, the fabrication of a preliminary patterned PLED array confirms their potential display applications.
materials science, multidisciplinary,optics