Removal of phosphorus and fluorine from wastewater containing PF 6 − via accelerated decomposition by Al 3+ and chemical precipitation for hydrometallurgical recycling of lithium-ion batteries

Takuto Miyashita,Kouji Yasuda,Tetsuya Uda

DOI: https://doi.org/10.1039/d3ew00854a

2024-04-03

Environmental Science Water Research & Technology

Abstract:During hydrometallurgical recycling of lithium-ion batteries (LIBs), one important challenge is the efficient treatment of wastewater containing LiPF 6 used as lithium salt in the LIBs. The difficulty of the treatment is attributed to the persistence of PF 6 − in aqueous solutions. In this study, the accelerated decomposition of PF 6 − by Al 3+ at an elevated temperature and the removal of phosphorus and fluorine by chemical precipitation were attempted. These reactions were analyzed by pH electrode, fluoride-ion selective electrode, distillation method for total fluorine analysis, ICP-AES, ion chromatography, XRD, and WDS. The results showed that when 10 mM LiPF 6 aqueous solution containing 100 mM Al 2 (SO 4 ) 3 was kept at 90 °C for 24 h, more than 90 % of the PF 6 − was decomposed into PO 4 3− and F − . The produced PO 4 3− and F − were coprecipitated with Ca 6 Al 2 (SO 4 ) 3 (OH) 12 (ettringite) by adding sufficient Ca(OH) 2 . The concentrations of total phosphorus and total fluorine in the supernatant after precipitation were 0.028 mM and 0.77 mM, respectively. Here, the pH after the decomposition of 10 mM PF 6 − decreases to around 1 due to the formation of H + during the decomposition, which may be too low for some practical cases. For this problem, the decomposition of PF 6 − in various pre-mixed solutions of Al 2 (SO 4 ) 3 and Ca(OH) 2 was also examined. As a result, when the prepared molar ratio was Al/Ca > 2/3, the decomposition of PF 6 − proceeded, and the pH decrease accompanying the decomposition was alleviated due to the buffer effect of Al(OH) 3 precipitate.

environmental sciences,engineering, environmental,water resources