Models for the decrease in ultimate elongation and embrittlement of organic coatings during degradation

Stuart G. Croll

DOI: https://doi.org/10.1016/j.porgcoat.2024.108271

IF: 6.6

2024-01-27

Progress in Organic Coatings

Abstract:Polymer organic coatings often become brittle, then crack and fail. Hypotheses are easily found for the chemical changes that cause embrittlement but not quantitative predictions for how the reduction in physical properties proceeds. During degradation, the ultimate elongation of a polymer coating diminishes substantially. The integrated mechanical strain energy density is a measure of toughness for ductile materials and appears in the derivation of the Griffith equation for brittle materials. This and a simple stochastic model for how the number of intact crosslink chains diminishes, used in the Lake-Thomas model for fracture energy, predicts that ultimate elongation decreases exponentially with exposure period, as literature data shows. Although failure initiates from defects, either natural to the heterogeneous structure of most coatings or from imperfections in application, increasing defect size with degradation does not appear to have a large effect on the exponential reduction of ultimate elongation; the major contributor is the reduction in intact crosslink chains. The Rouse model of polymer chain vibration modes demonstrates how dissipative relaxation mechanisms disappear with degradation, which also contributes to increasing brittleness.

materials science, coatings & films,chemistry, applied