Abstract:Mechanical property testing, spectral analysis, phase analysis, scattering evaluation and mechanism research of CFRP under various temperature and moisture composite environments. Temperature and moisture are important environmental conditions governing the usage of carbon fiber‐reinforced plastics (CFRP). In this study, tensile, compression, and shear tests of woven CFRP composites were conducted in four composite environments: cold‐temperature dry state, room‐temperature dry state, elevated‐temperature dry state, and elevated‐temperature wet state. Fourier transform infrared (FTIR) spectroscopy was used to analyze the molecular composition and structure under these environments. The fracture morphology was also analyzed using scanning electron microscopy (SEM) to understand the deterioration mechanism of the material properties at the macro and micro scales. Finally, a two‐parameter Weibull statistical model was used to evaluate the scattering of the composites. The results demonstrate that the tensile, compressive, and shear properties of the material decrease under harsh conditions, and the degradation effect on the ultimate strength is much greater than that of the modulus. Cold‐temperature dry and elevated‐temperature wet conditions are particularly severe. Composite environments significantly affect the macroscopic failure process and ultimate failure mode of materials. In general, the temperature and humidity of the matrix system acts at the core of the deterioration mechanism of composites, affecting the properties of the fiber/matrix and orthogonal woven fiber interfaces, and eventually resulting in a loss of their constitutive strength and bearing capacity. The theoretical ultimate strength were consistent with the experimental values. Highlights Comprehensive mechanical property testing in multiple composite environments. Degradation mechanisms were revealed from multiscale morphology analysis. Scattering of composites were evaluated using statistical analyses. Cold temperature dry and elevated temperature wet were the worst states. Deterioration effect of environment on matrix and interface is the core failure mechanism.

Durability and Prediction Models of Fiber-Reinforced Polymer Composites under Various Environmental Conditions: A Critical Review

Multi-Scale Modelling of Long-Term Mechanical Behaviour in Polymer Composite Laminates with Woven Fibre Architecture

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

A comprehensive review on mechanical properties of pultruded FRP composites subjected to long-term environmental effects

Review of aging mechanisms, mechanical properties, and prediction models of fiber‐reinforced composites in natural environments

Modeling of Load Responses and Aging of High Strength Fibers Considering UV-radiation

Modelling of Environmental Ageing of Polymers and Polymer Composites-Durability Prediction Methods

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Bond-Slip Models for FPR-Concrete Interfaces Subjected to Moisture Conditions

Fatigue Damage Assessment and Lifetime Prediction of Short Fiber Reinforced Polymer Composites—A Review

Durability of an Epoxy Resin and Its Carbon Fiber- Reinforced Polymer Composite upon Immersion in Water, Acidic, and Alkaline Solutions

Effect of temperature and moisture composite environments on the mechanical properties and mechanisms of woven carbon fiber composites

Review of Strain Rate Effects of Fiber-Reinforced Polymer Composites

Modeling and influencing factor analysis for the temperature and damage dependent tensile strength of fiber/polymer composites

The Aging Behavior and Life Prediction of CFRP Rods under a Hygrothermal Environment

Fatigue behavior and modeling of short fiber reinforced polymer composites: A literature review

Factors Affecting the Fatigue Behavior of Fiber-Reinforced Polymer Matrix Composites

Fatigue failure mechanism analysis and life prediction of short fiber reinforced polymer composites under tension-tension loading

Effect of seawater and stress coupling on the durability of carbon fibre-reinforced polymer