Synthesis of Nd-lean (Nd,Ce,La)-Fe-B magnets via hot deformation and rolling
K.S. Anand,E. Simsek,H. Huang,C. Pan,O. Palasyuk,R.P. Chaudhary,W. Tang,M.J. Kramer,J. Cui,R.T. Ott
DOI: https://doi.org/10.1016/j.jallcom.2024.176124
IF: 6.2
2024-09-13
Journal of Alloys and Compounds
Abstract:In this work, we have used bulk combinatorial synthesis to rapidly identify a (Nd,Ce,La)-Fe-B composition that is both Nd-lean (<50 % of total rare earth content) and exhibits good thermal stability ( TC ∼269 °C). Bulk anisotropic magnets of the corresponding composition [i.e. (Nd 0.47 Ce 0.28 La 0.25 ) 2.2 Fe 14 B 1 (at%) + (1.5 wt% TiC)] were synthesized by hot deformation and hot-roll processes. To enhance the energy product of the hot deformed alloys, feedstock powder with 2.5–7.5 wt% Ce-Al-Cu grain boundary modifier was blended together prior to deformation processing. Moreover, hot deformation processing parameters, temperature ( T ), and processing time ( t ), were examined over a wide range to enhance the energy product of the resultant magnet alloys. We found that adding just 2.5 wt% Ce-Al-Cu increased the maximum energy product from ∼12 MGOe for the monolithic alloy to ∼20 MGOe for the alloy with added grain bounder modifier. The processing parameters (e.g., temperature and time) identified for hot deformation were applied to the hot-rolling process to synthesize samples with larger dimensions that exhibit an energy product of 17.7 MGOe with 5 wt% Ce-Al-Cu added.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering