Abstract:Using CO2 polycarbonates as engineering thermoplastics has been limited by their mechanical performances, particularly their brittleness. Poly(cyclohexene carbonate) (PCHC) has a high tensile strength (40 MPa) but is very brittle (elongation at break <3%), which limits both its processing and applications. Here, well-defined, high molar mass CO2 terpolymers are prepared from cyclohexene oxide (CHO), cyclopentene oxide (CPO), and CO2 by using a Zn(II)Mg(II) catalyst. In the catalysis, CHO and CPO show reactivity ratios of 1.53 and 0.08 with CO2, respectively; as such, the terpolymers have gradient structures. The poly(cyclohexene carbonate)-grad-poly(cyclopentene carbonate) (PCHC-grad-PCPC) have high molar masses (86 < Mn < 164 kg mol-1, ĐM < 1.22) and good thermal stability (Td > 250 °C). All the polymers are amorphous with a single, high glass transition temperature (96 < Tg < 108 °C). The polymer entanglement molar masses, determined using dynamic mechanical analyses, range from 4 < Me < 23 kg mol-1 depending on the polymer composition (PCHC:PCPC). These polymers show superior mechanical performance to PCHC; specifically the lead material (PCHC0.28-grad-PCPC0.72) shows 25% greater tensile strength and 160% higher tensile toughness. These new plastics are recycled, using cycles of reprocessing by compression molding (150 °C, 1.2 ton m-2, 60 min), four times without any loss in mechanical properties. They are also efficiently chemically recycled to selectively yield the two epoxide monomers, CHO and CPO, as well as carbon dioxide, with high activity (TOF = 270-1653 h-1, 140 °C, 120 min). The isolated recycled monomers are repolymerized to form thermoplastic showing the same material properties. The findings highlight the benefits of the terpolymer strategy to deliver thermoplastics combining the beneficial low entanglement molar mass, high glass transition temperatures, and tensile strengths; PCHC properties are significantly improved by incorporating small quantities (23 mol %) of cyclopentene carbonate linkages. The general strategy of designing terpolymers to include chain segments of low entanglement molar mass may help to toughen other brittle and renewably sourced plastics.

Toughening CO2 -Derived Copolymer Elastomers Through Ionomer Networking

High-Efficiency Construction of CO2-Based Healable Thermoplastic Elastomers Via a Tandem Synthetic Strategy

High-Performance Olefin Thermoplastic Elastomer Based on Dynamically Cross-Linking Crystalline Macromers and Elastic Backbones

Highly Elastic and Degradable Thermoset Elastomers from CO2-based Polycarbonates and Bioderived Polyesters

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Aliphatic Polycarbonate Diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

Preparation Of Comb-Shaped Polyolefin Elastomers Having Ethylene/1-Octene Copolymer Backbone And Long Chain Polyethylene Branches Via A Tandem Metallocene Catalyst System

Modification of Poly(ethylene furandicarboxylate) with Aliphatic Polycarbonate diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

Poly(ethylene 2,5-Furandicarboxylate-mb-poly(tetramethylene Glycol)) Multiblock Copolymers: from High Tough Thermoplastics to Elastomers

CO2 Derived ABA Triblock All-Polycarbonate Thermoplastic Elastomer with Ultra-High Elastic Recovery

Controlled Carbon Dioxide Terpolymerizations to Deliver Toughened yet Recyclable Thermoplastics

A Topology‐Defined Polyester Elastomer from CO2 and 1,3‐butadiene: A One‐Pot‐One‐Step “scrambling Polymerizations” Strategy

A Facile Approach to Construct Novel Polyesters as Soft Midblock for Thermoplastic Elastomers

CO2-Based Block Copolymers: Present and Future Designs

Metal-Free Synthesis of Biodegradable CO2-Based Oligo(carbonate-ester) Diols As Building Blocks for Thermoplastic Polyurethanes

Construction of CO2‐based thermoplastic elastomer via combining aliphatic polycarbonate and polyamide: A multiblock copolymer PPC‐mb‐PA6

Supersoft Norbornene‐Based Thermoplastic Elastomers with High Strength and Upper Service Temperature

Preparation and Characterization of High Melt Strength Thermoplastic Polyester Elastomer with Different Topological Structure Using a Two-Step Functional Group Reaction

High-Performance Polyethylene-Ionomer-Based Thermoplastic Elastomers Exhibiting Counteranion-Mediated Mechanical Properties

Toward Sustainable and Strong ABA-Type Thermoplastic Elastomers with Poly(-Caprolactone-<i>co</i>-4-Methyl--Caprolactone) Soft Midblock and Polystyrene Hard End Blocks

High Molar Mass Polycarbonates as Closed-Loop Recyclable Thermoplastics

Mechanical and Rheological Properties and CO2-foaming Behavior of Reactively Modified TPEE with Controlled Chain Entanglement