Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Nondestructive analysis of rolling contact fatigue cracks using induced scanning thermography

Rolling Contact Fatigue Detection Using Eddy Current Pulsed Thermography

Research on Eddy Current Pulsed Thermography for Rolling Contact Fatigue Crack Detection and Quantification in Wheel Tread

Analysis of the RCF crack detection phenomenon based on induction thermography

Characterization of Rolling Contact Fatigue Cracks in Rails by Eddy Current Pulsed Thermography

The Early Stage Wheel Fatigue Crack Detection Using Eddy Current Pulsed Thermography

Depth quantification of rolling contact fatigue crack using skewness of eddy current pulsed thermography in stationary and scanning modes

Analysis on asymmetrical RCF cracks characterisation using an ACFM sensor and the influence of the rail head profile

RCF crack direction assessment in moving ferromagnetic material by DC electromagnetic NDT technique

Dynamic Electromagnetic Thermography System for Rail Inspection

Detection of Closed Cracks on the Rail Surface in Thermography NDT

Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects

3D photothermal reconstruction of subsurface defects in notched multidirectional CFRP laminates due to tensile fatigue loading

Pulsed Air-Flow Thermography for Natural Crack Detection and Evaluation

Rail rolling contact fatigue formation and evolution with surface defects

Experimental study on wheel-rail rolling contact fatigue damage starting from surface defects under various operational conditions

Induction Infrared Thermography and Thermal-Wave-Radar Analysis for Imaging Inspection and Diagnosis of Blade Composites

Robot‐assisted crack detection on complex shaped components using constant‐speed scanning infrared thermography with laser line excitation

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Exploratory Factor Analysis for Defect Identification with Active Thermography

Evaluation of typical rail defects by induction thermography: experimental results and procedure for data analysis during high-speed laboratory testing