Assessment of Changes in Abrasive Wear Resistance of a Welded Joint of Low-Alloy Martensitic Steel Using Microabrasion Test

Krzysztof Ligier,Jerzy Napiórkowski,Magdalena Lemecha

DOI: https://doi.org/10.3390/ma17092101

IF: 3.4

2024-04-30

Materials

Abstract:Martensitic low-alloy steels are widely used in machine construction. Due to their declared weldability, arc welding is most often used to join elements made of this type of steel. However, the high temperature associated with welding causes unfavourable changes in the microstructure, resulting in reduced abrasion resistance. Therefore, it is important to know the tribological properties of the welded joint. This article presents the results of a study on the abrasion wear resistance of a welded joint of an abrasion-resistant steel. This study tested a welded joint of an abrasive-resistant steel produced by the arc welding method. Wear testing of the welded joint was carried out under laboratory conditions by the ball-cratering method in the presence of abrasive slurry on the cross-section of the welded joint. Based on the test results, the change in the abrasive wear rate of the material as a function of the distance from the welded joint axis was determined. It was also found that the thermal processes accompanying welding caused structural changes that increased the wear rate index value. Adverse changes in the tribological properties of a welded material persist up to a distance of approx. 20 mm from the weld centre.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

### Problems Addressed by the Paper

The paper primarily explores the impact of the welding process on the wear resistance of weld joints in low-alloy martensitic steel. Specifically, the paper aims to evaluate how the thermal effects accompanying the welding process alter the microstructure of the material, thereby affecting its wear resistance. The study analyzes the wear performance of different regions of the weld joint through micro-wear tests (ball crater method).

### Main Findings
1. **Hardness Variation**: The hardness in the welding area significantly decreases, especially in the weld zones (WZ-1 and WZ-2), where the hardness is approximately one-fourth of the base material's hardness.
2. **Wear Resistance Variation**: The wear resistance in the weld zone is the poorest, with the wear rate index being 5 to 8.5 times higher than that of the base material. The wear resistance in the heat-affected zone (HAZ) also fluctuates, with a sudden drop in wear resistance near the weld zone, followed by an increase approximately 9 millimeters from the weld center.
3. **Microstructure Changes**: The high temperatures induced by welding cause changes in the material's microstructure, primarily in the weld zone and the heat-affected zone. These microstructural changes directly affect the material's hardness and wear resistance.
4. **Applicability of Testing Method**: The ball crater method can be used to accurately assess the wear resistance of different regions of the weld joint.

Overall, the study reveals the impact of the thermal effects accompanying the welding process on the wear resistance of weld joints in low-alloy martensitic steel and validates the effectiveness of the ball crater method in evaluating this impact.