Abstract:Increased ethylene formation during vapor‐fed carbon dioxide reduction is achieved by employing tandem electrocatalyst consisting of nickel‐coordinated nitrogen‐doped carbon and cuprous oxide, which act as carbon monoxide generator and coupler, respectively. Performance evaluation is conducted in both flow electrolyte and membrane electrode assembly electrolyzers to demonstrate the potential for large‐scale and direct carbon dioxide gas conversion into value‐added chemicals. Ethylene is particularly attractive due to its major importance as a feedstock for various applications including the polymer industry. As such, catalyst and electrolyzer developments are crucial to achieve industrially relevant ethylene production and efficiency levels. Here, a tandem electrocatalyst composed of copper nanocubes and nickel‐coordinated nitrogen‐doped carbon (NiNC) is presented, which is integrated into gas diffusion electrodes (GDEs) for direct conversion of vapor‐fed CO2 into ethylene. Evaluation of tandem GDEs in the vapor‐fed flow electrolyzer shows significantly increased ethylene selectivity in terms of faradaic efficiency and C2H4/CO ratio compared to a non‐tandem copper GDE. The enhancements are attributed to the increased local CO availability near the copper surface via effective CO2 to CO conversion on neighboring NiNC. The experimental results are validated by 3D resolved continuum simulations, which show increased flux of higher‐order products with the added CO flux from NiNC. The practical viability of Cu/NiNC catalyst is further evaluated in a membrane electrode assembly electrolyzer, achieving 40% FE toward ethylene at 150 mA cm−2 and 3.2 V. These findings highlight the high selectivity and formation rate of ethylene achieved by successful device integration of the Cu/NiNC catalyst, demonstrating the potential for implementation in large‐scale sustainable CO2 electrolyzers.

Selective Ethylene Production from CO2 and CO Reduction via Engineering Membrane Electrode Assembly with Porous Dendritic Copper Oxide

Efficiently Electroreducing CO2 to Ethylene on Heterostructured CeO2/CuO

Carbon‐Efficient CO2 Electrolysis to Ethylene with Nanoporous Hydrophobic Copper

High-Rate and Efficient Ethylene Electrosynthesis Using a Catalyst/Promoter/Transport Layer

Continuous Carbon Dioxide Electroreduction to Concentrated Multi-carbon Products Using a Membrane Electrode Assembly

Efficient Ethylene Electrosynthesis Through C–O Cleavage Promoted by Water Dissociation

High‐rate and Selective CO2 Electrolysis to Ethylene via Metal‐Organic Framework‐augmented CO2 Availability

CO Electrolysis to Multicarbon Products over Grain Boundary-Rich Cu Nanoparticles in Membrane Electrode Assembly Electrolyzers

Temperature-dependent selectivity for CO electroreduction on copper-based gas-diffusion electrodes at high current densities

Ethylene Production from Carbonate Using a Bipolar Membrane Electrolysis System

Selective, Stable Production of Ethylene Using a Pulsed Cu-Based Electrode

Morphology-Directed Selective Production of Ethylene or Ethane from CO2 on a Cu Mesopore Electrode

Cascade CO2 electroreduction enables efficient carbonate-free production of ethylene

Vapor‐Fed Electrolyzers for Carbon Dioxide Reduction Using Tandem Electrocatalysts: Cuprous Oxide Coupled with Nickel‐Coordinated Nitrogen‐Doped Carbon

Electrochemical Reduction of CO2: A Common Acetyl Path to Ethylene, Ethanol or Acetate

Stabilized Cu0 -Cu1+ dual sites in a cyanamide framework for selective CO2 electroreduction to ethylene

Localized Alkaline Environment via In Situ Electrostatic Confinement for Enhanced CO2-to-Ethylene Conversion in Neutral Medium

Efficient electrocatalytic CO2 reduction to ethylene using cuprous oxide derivatives

Converting CO 2 to multi-carbon products at >1 A/cm 2 using gas diffusion electrode based on commercial materials via transfer process engineering

Selective CO2 Reduction to Ethylene Mediated by Adaptive Small‐molecule Engineering of Copper‐based Electrocatalysts

Preferential Formation of Ethylene Via Electrocatalytic CO2 Reduction on Mesoporous Cu2O Nanoparticles: Synergistic Effects of Pore Structure Confinement and Surface Amine