Abstract:Journal of Composite Materials, Ahead of Print. Carbon fiber/epoxy composites (CFRP) are nowadays extensively used in aircraft structures. During the lifecycle of an aircraft, composites are subjected to temperature and humidity variation over time and that can lead to performance loss. Efforts to understand the environmental conditioning impact on CFRP properties have been widely investigated, leading to the main objective of this study, which was investigating whether damages caused by different environmental conditioning individually are intensified when they are combined. During an aircraft lifetime, several different environmental conditions may occur, and to simulate these effects, this research tested coupons that were exposed to long-term hygrothermal conditioning, drying and thermal cycling and their combined effects on fracture toughness in mode-I and mode-II. Dynamic mechanical and fractographic analysis were also performed on the specimens. Thermal cycling on unaged samples (reference) resulted in average reductions of 5% and 15%, for mode-I and mode-II fracture toughness, respectively, compared to the reference samples. Furthermore, combined effect of thermal cycling and hygrothermal conditionings resulted in reductions around 44% (mode-I) and 15% (mode-II) compared to the reference. The combination of different environmental conditionings was more detrimental to fracture toughness in Mode-I, as confirmed by fractographic analysis. In contrast, Mode-II showed no change in results when exposed to a combination of conditionings, suggesting that isolated analysis of the results can be misinterpreted. Combined effects of thermal cycling and hygrothermal conditioning affected fracture toughness more than either effect alone. Mode-I testing proved to be more sensitive to identifying environmental exposure effects on properties than mode-II.

Effect of low temperature on interlaminar fracture toughness of multi-directional CFRP and CFRP-steel interfaces

The influence of temperature and moisture on the mode I fracture toughness and associated fracture morphology of a highly toughened aerospace CFRP

A multi-linear constitutive relation considering the temperature effect on quasi-static mode I delamination in UD/MD laminates

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Effect of fiber orientation of adjacent plies on the mode I delamination fracture of carbon fiber reinforced polymer multidirectional laminates

Revealing low temperature-mechanical coupling failure mechanisms in CFRP laminates with in-situ observations

A comprehensive experimental investigation of the rate-dependent interlaminar delamination behaviour of CFRP composites

Investigation of flexure response and damage behavior of CFRP/aluminum hybrid laminates among various temperatures

Translaminar enveloping ply for CFRP interlaminar toughening

Bolt-bearing behavior of hybrid CFRP-steel laminates at low temperature

Evaluating the loading rate dependency of mode I delamination for composite laminates at different temperatures

Internal shear damage evolution of CFRP laminates ranging from -100°C to 100°C using in-situ X-ray computed tomography

Decomposing the coupling damage in mode I multidirectional delamination

Effect of temperature variation on the plate-end debonding of FRP-strengthened steel beams: coupled mixed-mode cohesive zone modeling

Mode II Interfacial Fracture Characterization of Foam Core Sandwich Materials at Elevated Temperatures: the Effects of Frictional Stresses Between the Crack Edges

Interlaminar toughening in structural carbon fiber/epoxy composites interleaved with carbon nanotube veils

Study on interlaminar performance of CNTs/epoxy film enhanced GFRP under low-temperature cycle

Influence of the combined effect of long hygrothermal aging and thermal cycling on mode I and II interlaminar fracture toughness of carbon/epoxy composites

Fracture toughness and fiber bridging mechanism for mode-I interlaminar failure of spread-tow woven composites

Experimental Study on Effect of Fiber Angel Orientation and Mixed-Mode Ratio on Fracture Toughness of Fiber Reinforced Laminate

Cohesive Zone Modeling of the Interface Fracture in Full-Thermoplastic Hybrid Composites for Lightweight Application