Abstract:This study has investigated the structure and mechanical properties of pure Zr and a series of binary Zr–Ti alloys in order to determine their potential application as dental implant materials. The titanium contents of these alloys range from 10 to 40wt.% and were prepared by arc melting in inert gas. This study evaluated the phase and structure of these Zr–Ti alloys using an X-ray diffraction (XRD) for phase analysis, and an optical microscope for microstructure analysis of the etched alloys. Three-point bending tests were performed to evaluate the mechanical properties of all specimens. The experimental results indicated that the pure Zr and Zr–10Ti comprised entirely of an acicular hexagonal structure of α′ phase. When the Ti content increased to 20wt.%, a significant amount of β phase was retained. However, when the Ti content increased to 40wt.%, only the equi-axed, retained β phase was observed in the cast alloy. Moreover, the hardness values and bending strengths of the Zr–Ti alloys decreased with an increasing Ti content. Among pure Zr and Zr–Ti alloys, the α′-phase Zr–10Ti alloy has the greatest hardness and bending strength. The pure Zr and Zr–Ti alloys exhibit a similar elastic modulus ranging from 68GPa (Zr–30Ti) to 78GPa (Zr–40Ti). Based on the results of elastic moduli, pure Zr and Zr–Ti alloys are found to be suitable for implant materials due to lower modulus. Like bending strength, the elastically recoverable angle of Zr–Ti alloys decreased as the concentration of Ti increased. In the current search for a better implant material, the Zr–10Ti alloy exhibited the highest bending strength/modulus ratios as large as 25.3, which are higher than that of pure Zr (14.9) by 70%, and commercially pure Ti (8.7) by 191%. Thus, Zr–Ti alloy's low modulus, ductile property, excellent elastic recovery capability and impressive strength confirm that it is a promising candidate for dental implant materials.

The effect of the solute on the structure, selected mechanical properties, and biocompatibility of Ti–Zr system alloys for dental applications

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Development and properties of dental Ti–Zr binary alloys

Microstructure, mechanical properties, and preliminary biocompatibility evaluation of binary Ti–Zr alloys for dental application

The structure and mechanical properties of as-cast Zr–Ti alloys

Biocompatibility and Osteogenic Activity of Zr?30Ta and Zr?25Ta?5Ti Sintered Alloys for Dental and Orthopedic Implants

Titanium-Zirconium Binary Alloy as Dental Implant Material: Analysis of the Influence of Compositional Change on Mechanical Properties and In Vitro Biologic Response.

Effects of Zr Addition on the Microstructural Evolution, Mechanical Properties, and Corrosion Behavior of Novel Biomedical Ti-Zr-Mo-Mn Alloys.

Cytocompatibility of Ti–xZr Alloys As Dental Implant Materials

Microstructure and Mechanical Properties of Ti-Zr-Cr Biomedical Alloys.

Cytocompatibility, Stability and Osteogenic Activity of Powder Metallurgy Ta-xZr Alloys As Dental Implant Materials

Suitability of Ti–Zr Alloy for Dental Implants: Tribocorrosion Investigation

Effects of Zirconium on mechanical and electrochemical properties of Ti-15mo alloy for biomedical applications

The Effect of Zr Content on the Microstructure, Mechanical Properties and Cell Attachment of Ti-35nb-Xzr Alloys

The Effect of Solution Heat Treatment Time on the Phase Formation and Selected Mechanical Properties of Ti-25Ta-xZr Alloys for Application as Biomaterials

Microstructure, Mechanical Properties and Corrosion Behaviors of Biomedical Ti-Zr-Mo-xMn Alloys for Dental Application

Mechanical Characterisation and Biomechanical and Biological Behaviours of Ti-Zr Binary-Alloy Dental Implants

Bone Response in Vivo of Ti-45Zr Alloy As Dental Implant Material

Vacuum sealing-assisted processing of titanium–zirconium alloys: synthesis, microstructure, hardness, friction, wear, and corrosion studies for biomedical application

Microstructure, Mechanical Properties, Castability and in Vitro Biocompatibility of Ti-Bi Alloys Developed for Dental Applications.

Modifications of Titanium and Zirconium Alloy Surfaces for Use as Dental Implants