Abstract:Ti-6Al-4 V (Ti(V)) is a biocompatible material with good mechanical properties, widely used as an implant in dental and orthopedic applications. However, it is susceptible to corrosion when it is in contact with the human body and mouth environment. To overcome this drawback and enhance its use in dental applications, we functionalized this alloy using Atomic Layer Deposition (ALD). Thin films of TiO2 and ZrO2 were deposited on polished Ti(V) discs by ALD as single and mixed oxides. Four groups were characterized: non-deposited Ti(V) (control); TiO2 deposited; ZrO2 deposited; mixed TiO2/ZrO2 film with 1:4 thickness ratio (TZO). ALD precursors and oxidizer were tetrakis(dimethylamido)titanium, tetrakis(dimethylamido)zirconium, and ozone, respectively. The existence and composition of each coating were confirmed with x-ray photoelectron spectroscopy. Electrochemical tests were performed in artificial saliva solution at 37 ± 1 °C to investigate the corrosion behavior of the surface in simulated oral conditions. The corrosion rate was decreased by over 64 % on the coated samples compared to the control. The surface roughness and morphology of the areas were analyzed before and after corrosion using optical profilometry, scanning electron microscopy (SEM), and energy-dispersive x-ray spectroscopy (EDS), respectively. The surface roughness and topography of the samples did not change significantly after the corrosion. However, the SEM and EDS results revealed that the TZO group had the best surface protection against corrosion compared to the control and either of single oxides. The results of this study indicated that having a combination of TiO2 and ZrO2 in the form of an ultra-thin film with a thickness of ~30 nm would provide protection of Ti(V) surfaces in artificial saliva, thereby enhancing the dental implant robustness and lifetime in the aggressive oral environment, and therefore increasing patient satisfaction.

[Neurogenic ectopic ossification: a physiatry update].

Corrosion Resistance of Passive Film Formed on TA10 Dental Implant in Simulated Body Fluid

Biomechanical comparison of biomimetically and electrochemically deposited hydroxyapatite-coated porous titanium implants.

In vitro corrosion behavior of coated Ti6Al4V with TiO2, ZrO2, and TiO2/ZrO2 mixed nanofilms using atomic layer deposition for dental implants

Electrochemical corrosion study of chitosan-hydroxyapatite coated dental implant

Effect of PMMA sealing treatment on the corrosion behavior of plasma electrolytic oxidized titanium dental implants in fluoride-containing saliva solution

Structural characterization, mechanical, and electrochemical studies of hydroxyapatite-titanium composite coating fabricated using electrophoretic deposition and reaction bonding process.

Investigating the Concurrent Effect of Cerium/Hydroxyapatite Coatings on Mg-Based Implant for Enhancing Corrosion Performance and In-Vitro Activity

Corrosion and biological study on biofunctionalized porous coating on titanium produced by plasma electrolytic oxidation

Effects of open circuit immersion and vertex potential on potentiodynamic polarization scans of metallic biomaterials

Effects of Hydrogen Peroxide Concentration and Heat Treatment on the Mechanical Characteristics and Corrosion Resistance of Hydroxyapatite Coatings

In-vitro corrosion performance of hydroxyapatite-coated Al2024 in simulated body fluid: A comparative study

Clinical Evaluation of Corrosion Resistance, Ion Release, and Biocompatibility of CoCr Alloy for Metal-Ceramic Restorations Produced by CAD/CAM Technologies

Exploring the effect of chlorhexidine concentration on the biocorrosion behavior of Ti6Al4V for dental implants

[Treatment results of perforating eye injuries (a clinical statistical study) (author's transl)].

In vitro electrochemical evaluation and phase purity of natural hydroxyapatite coating on medical grade 316L stainless steel

The effect of silver nanoparticles on biological and corrosion behavior of electrophoretically deposited hydroxyapatite film on Ti6Al4V

An Insight on Corrosion Resistance Ability of Biocompatible Dental Implants through Electrochemical Impedance Spectroscopy

The electrochemical behavior and surface analysis of Ti<sub>49.6</sub>Ni<sub>45.1</sub>Cu<sub>5</sub>Cr<sub>0.3</sub>alloy for orthodontic usage

Health care developments to achieve healthy aging and longevity in super-aged society.

Electrochemical Deposition of Hydroxyapatite Co-Substituted By Sr/Mg Coating on Ti-6Al-4V ELI Dental Alloy Post-MAO as Anti-Corrosion