An analysis of the microstructure of the heat-affected zone of an ultra-low carbon and niobium-bearing acicular ferrite steel using EBSD and its relationship to mechanical properties
Aimin Guo,R.D.K. Misra,Jibin Liu,Ling Chen,Xinlai He,S.J. Jansto
DOI: https://doi.org/10.1016/j.msea.2010.06.092
2010-01-01
Abstract:We describe here the microstructure of simulated thermal cycles with the different peak temperatures associated with the heat-affected zone (HAZ) in a 600 MPa acicular ferrite steel. The microstructure, crystallographic features, and the effective grain size of different regions in the HAZ were examined by transmission electron microscopy (TEM) and electron back scattering diffraction (EBSD) analysis. The study indicated that the effective grain size decreases with decrease in peak temperature and attains the smallest value at a peak temperature of 900 °C. However, EBSD analysis indicated that the effective grain size of the sub-zones is small, which contributes to the excellent low temperature toughness in the sub-zones of HAZ. Two hardness peaks were observed at temperatures of 800 °C and 1200 °C because of grain refinement. The study convincingly demonstrates that EBSD can accurately identify the effective grain size contribution on complex and fine-grained microstructures, and is helpful in predicting the grain refinement mechanism. Keywords Steels EBSD Heat-affected zone (HAZ) Grain refinement Acicular ferrite 1 Introduction Grain refinement continues to be an important and viable approach to obtain high strength–high toughness combination. Thus, an accurate measurement of the effective grain size is important to study the mechanism of grain refinement. For diffusion-controlled ferrite–pearlite microstructure under high temperature equilibrium conditions, the size of ferrite grains represents the actual grain size, i.e. the effective grain size. However, it is difficult to determine the effective grain size of the intermediate transformation microstructures, such as acicular ferrite, bainite, and martensite, particularly, if the phase transformation is rapid and shear-controlled, and a complex microstructure is obtained. Electron back scattered diffraction (EBSD) in SEM enables determination of phase and crystallographic orientation of the sample in different regions by recording diffraction patterns along the sample surface in steps of defined size [1–3] . The size and relative location of grain boundaries, phases, and grains in the sample can be conveniently determined using crystallographic information [4] . Extensive studies have been carried out to improve the toughness of the weld metal and/or HAZ of steels [5–9] . Given the fact that the microstructure of weld and heat-affected zone (HAZ) plays an important role in defining the mechanical properties of the weld zone [10–12] , a number of studies predicted the effect of microstructure and mechanical properties of weld zone and HAZ in steels [13–15] . A weld thermal cycle simulation technique was employed to examine the transformation behavior of the HAZ in the microalloyed steels, where the HAZ was generally divided into fusion zone, grain-coarsened zone, grain-refined zone, and partially transformed zone. Although the sub-zones in the HAZ experienced complicated thermal cycles during the actual welding process, they can, however, be simulated by the right choice of the peak temperatures. In an attempt to understand the strengthening and toughening mechanisms in the HAZ of an ultra-low carbon acicular ferrite steel, simulation of thermal cycle with different peak temperatures associated with different sub-zones of heat-affected zone (HAZ) was studied by EBSD in terms of microstructure and effective grain size in sub-zones of the HAZ. 2 Experimental procedure A 600 MPa ultra-low carbon acicular ferrite steel of 50 mm thickness was produced by an advanced TMCP-RPC (Thermal-Mechanical Controlled Processing-Relaxed Precipitation Control) process. The processing of the steel was carried out as follows: The reduction of the slab was greater than 50% in the two stages. The first stage was completed above 900 °C and the plate was held for several seconds after the second stage rolling. The plate was then water-cooled to 500 °C and subsequently cooled to the room temperature in air. Detailed processing details are not given here because of proprietary reasons. The chemical composition of the steel is presented in Table 1 . The peak temperatures ( T m ) for thermal cycle simulation in Gleeble 2000 were in the range of 800–1400 °C to simulate the different regions in HAZ. The Gleeble specimens had dimensions of 10 mm × 12 mm. Specimens were polished using standard metallographic procedures and etched with 3 vol.% Nital. EBSD analysis was conducted using a Quanta 400 operated at 30 kV. 3 Results 3.1 Microstructure of the HAZ sub-zones Fig. 1 shows the light micrographs of the sub-zones in HAZ simulated using different peak temperatures with the t 8/5 = 20 s (the time for temperature to drop from 800 °C to 500 °C). It is observed that at the peak temperature of 800 °C, the rolling characteristics disappear because of the occurrence of a small content of recrystallized microstructure ( Fig. 1 a). At the peak temperature of 1000 °C ( Fig. 1 b), a significant content of fine ferrite is formed because of complete recrystallization. With subsequent increase in peak temperature, the austenite grain size was increased and transformed to bainite during the cooling. At 1400 °C, the microstructure primarily consisted of bainitic lath together with acicular ferrite with the original austenite grains of average grain size of 60 μm ( Fig. 1 d). The TEM micrographs corresponding to the peak temperature of 1400 °C and 1200 °C are presented in Fig. 2 , respectively. Retained austenite and/or M/A constituents were present at the sub-grain boundary of bainite lath at the peak temperature of 1400 °C ( Fig. 2 a and b). Widmanstätten ferrite ( Fig. 2 c) grew from the grain boundary and acicular ferrite ( Fig. 2 d) formed in the interior of the austenite grain. At the peak temperature of 1400 °C, the austenite grains coarsened and indicated a high content of grain boundary and intragranular acicular ferrite compared to that at the peak temperature of 1200 °C. However, the latter indicated wide bainitic lath and higher content of M/A constituent. Compared to the traditional ultra-low carbon lath bainitic steel, a significantly higher acicular ferrite is formed in the austenite grain, which is responsible for good low temperature toughness (see below). In Fig. 3 , TEM micrographs at the peak temperature of 900 °C consisting of massive ferrite and grain boundary features are presented. The massive ferrite has curved grain boundaries and low dislocation density. In contrast to the behavior at 900 °C ( Fig. 3 ), the microstructure at 800 °C consists of acicular ferrite, partially recrystallized microstructure, incomplete recrystallized massive ferrite and M/A constituent ( Fig. 4 a–d ). In Fig. 5 a is presented impact toughness as a function of peak temperature for the sub-zones of HAZ simulated specimens corresponding to different peak temperatures with the t 8/5 = 20 s. The toughness is lowest at the peak temperature of 800 °C and is highest at the peak temperature of 600 °C and 700 °C when tempering is rapid at these temperatures. The toughness is high at the peak temperature of 900 °C and 1100 °C, but decreases at the peak temperatures of 1200 °C and 1400 °C. In Fig. 5 b, the Vickers hardness data of the sub-zones is presented. It can be seen that there are two peaks at 216 HV 10 and 225 HV 10 , respectively at the peak temperature of 800 °C and 1200 °C. The hardness of 194 HV 10 at the peak temperature of 900 °C is close to that of the base matrix, and is discussed later. The EBSD analysis of the microstructural features of the sub-zones of HAZ simulated specimens corresponding to different peak temperature is presented in Fig. 6 a–f . At the peak temperature of 1400 °C ( Fig. 6 a), the microstructure primarily consists of ferrite lath, which divides the original austenite grain into separate regions together with small amount of acicular ferrite. At the peak temperature of 1200 °C ( Fig. 6 b), the microstructure consists of acicular ferrite and some granular bainite. The microstructure corresponding to 1000 °C ( Fig. 6 c) and 900 °C ( Fig. 6 d) is irregular ferrite and equiaxed ferrite, respectively. At the peak temperature of 800 °C ( Fig. 6 e), the microstructure is a complex mixture of acicular ferrite of the base metal, massive ferrite, and a small amount of fine equiaxed ferrite obtained from the incomplete recrystallization. 3.2 Effective grain size of simulated sub-zones Fig. 7 a–d shows the grain growth features and distribution of effective grain size of simulated sub-zones. At the peak temperature of 800 °C, the effective grain size is 7.73–8.83 μm ( Fig. 7 a) and the statistical distribution of grain size indicates non-uniform microstructure because of partial recrystallization. The effective grain size was smallest (3.95–4.17 μm) at the peak temperature of 900 °C ( Fig. 7 b) and increased with peak temperature. The grain size distribution at the peak temperature of 1200 °C indicated that the prior austenite grains started to grow such that the effective grain size was 8.12–9.36 μm ( Fig. 7 c). At the peak temperature of 1400 °C, austenite grains grow fast and there was bimodal grain size distribution ( Fig. 7 d). The effective grain size of simulated sub-zones is summarized in Table 2 for 20 fields of view for each specimen with grain angles set as 10° and 15°, respectively. 3.3 EBSD analysis on the angles between neighboring grains The angles between neighboring grains of the specimens at different peak temperatures were examined by EBSD with a resolution of 2°. The EBSD analysis map and statistical distribution of the grain angles between adjacent grains for different temperatures are presented in Figs. 8a–d and 9a–d , respectively. In these figures, different colors represent different grain boundary angles, for example, green standing for smaller angles of 3–12°, blue for 12–22°, red for 22–32°, purple for 32–42°, yellow for 42–52°, and white for 52–62°. It is observed that the incomplete recrystallization zone at the peak temperature of 800 °C was smallest by the grain boundary angle ( Figs. 8a and 9a ), followed by 1200 °C ( Fig. 8c and 9c ) and 1400 °C ( Figs. 8d and 9d ). At the peak temperature of 900 °C ( Figs. 8b and 9b ), the number of small-angle grain boundaries was significantly reduced and grains with large angles dominated the microstructure. In Table 3 , a summary of the proportion of grain boundaries with different grain boundary angles is presented. It can be concluded from Table 3 that the strength should be maximum at the peak temperatures of 800 °C and 1200 °C, and the former should have higher strength because of sub-grain strengthening. (For interpretation of references to color in Figs. 8 and 9, the reader is referred to the web version of this article.) 4 Discussion 4.1 Microstructure of sub-zones in HAZ The weld thermal cycle simulation technique was employed to examine the transformation behavior of the HAZ in the microalloyed steels. As we know that the HAZ can generally be divided into fusion, grain-coarsened, grain-refined and partially transformed zones. These sub-zones can be simulated by means of different peak temperature. The experimental phase transformation temperatures, A c1 and A c3 are 710 °C and 860 °C, respectively. The temperatures of 1400 °C and 1200 °C correspond to the coarse-grained region in HAZ and temperatures of 900 °C and 800 °C are related to the recrystallization phase zone and incomplete recrystallization phase zone, respectively. At the peak temperature of 1400 °C, the austenite grains coarsen compared to 1200 °C and the transformed microstructure shows a higher amount of intragranular acicular ferrite and Widmanstäten ferrite ( Fig. 2 ). However, dominant microstructures are bainitic lath and acicular ferrite. Compared to traditional ultra-low carbon bainitic steel, significantly higher acicular ferrite formed in the austenite grain is expected to provide good low temperature toughness. At the peak temperature of 900 °C, complete recrystallization occurred at high-energy positions such as grain boundary interfaces with consequent formation of fine idiomorphic grains. However, incomplete recrystallization occurred at the low-energy positions in the form of massive ferrite with low dislocation density. At the peak temperature of 800 °C, between the A c1 and A c3 , the recrystallization occurred only at the high-energy positions, i.e. at the austenite grain boundary. The microstructure consisted of retained acicular ferrite and massive ferrite with M/A constituents. 4.2 Evaluation of the grain refinement mechanisms of sub-zones in HAZ In the case of mixed microstructure of high strength steels, the formation of domains leads to microstructural refinement. Domain is defined as a cell with misorientation angle larger than 10° between neighboring grains in the deformed austenite and represents the effective grain size of the fine-grained microstructure in steels. The identification of the effective grain size is difficult. In the present work, the effective grain size in the mixed microstructure was identified by EBSD analysis technique, and the microstructural features and effective grain size were analyzed in the sub-zones in HAZ. Fig. 10 shows variation of the effective grain size with peak temperature with the grain angles set as 10° and 15°. It is observed that the variant of the actual grain size is consistent with the peak temperature. At the peak temperature of 1400 °C, the microstructure in the fusion line was characterized by largest effective grain size of 9.83–11.41 μm, and was similar to the microstructure at the peak temperature of 1200 °C with the effective grain size of 9.89–11.39 μm, which is in the low-temperature region of coarse-grained zone. The effective grain size reduces with decrease in temperature and is smallest at the peak temperature of 900 °C (i.e. 3.95–4.17 μm). However, when the temperature is 800 °C, the effective grain size increases to 7.73–8.83 μm. It can be concluded that the effective grain size of the sub-zones varies within the smaller range, even though the microstructure is coarse in the coarse-grain zone, which suggests the reasons why the weld joints have excellent low temperature toughness in the sub-zones in HAZ in ultra-low carbon acicular ferrite steel. In Fig. 11 , the percentage of large-angle grain boundary with different neighboring grain angles is presented for different peak temperatures. It is observed that the variance of the percentage of large-angle grain boundary for different peak temperatures is similar with the neighboring grain angles set in the range of 5–40°. The growth of austenite grains in the coarse-grain zone is not very obvious, as shown in Fig. 11 . 4.3 The effect of low angle grain boundary on hardening of weld joint microstructure The relationship between low angle grain boundary and the peak temperatures is presented in Fig. 12 , with first maxima at 800 °C and second maxima at 1200 °C, consistent with the hardness variance with temperature. This can be explained as follows. The temperature of 800 °C corresponds to the ferrite–austenite region when the microstructure is a combination of acicular ferrite retained from the base metal and massive ferrite transformed from the partially austenitic zones. There are also many M/A constituents in the massive ferrite. Lath with the neighboring grain angle smaller than 3° is retained in acicular ferrite with high density of dislocations located among these laths. Therefore, there is a large quantity of small-angle grain boundaries between neighboring grains. The peak temperature of 1200 °C is at the junction of coarse-zone and completely recrystallized zone. The lath features in this zone are distinct than that of completely recrystallized zone and the microstructure is finer as compared to that at 1400 °C, which is responsible for the hardness peak at this peak temperature. It is demonstrated that the ratio of the low angle grain boundary set as 3° reflects the amount of the lath and the level of refinement. Accordingly, it can be concluded that the grain refinement leads to the appearance of the peak hardness values at peak temperatures of 800 °C and 1200 °C. 5 Conclusions a. Effective grain size decreased with decrease in the peak temperature and attained the smallest value at 900 °C. However, when the temperature was decreased to 800 °C, the effective grain size started to increase. b. Effective grain size of the sub-zones of the investigated steel is small, which is responsible for the excellent low temperature toughness in the sub-zones in HAZ. c. The formation of acicular ferrite (AF) in the sub-zones (CGHAZ) plays an important role in the refinement of CGHAZ. d. EBSD can be used to identify the grain size contribution of complex fine-grained microstructure. References [1] H. Kitahara R. Ueji M. Ueda N. Tsuji Y. Minamino Mater. Charact. 54 2005 378 386 [2] F.J. Humphreys J. Mater. Sci. 36 2001 3833 3854 [3] V. Randle Microtexture Determination and its Applications second ed. 2003 Institute of Materials/Maney London [4] K.P. Mingard B. Roebuck E.G. Bennett M.G. Gee H. Nordenstrom G. Sweetman P Chan J. Refract. Met. Hard Mater. 27 2009 213 223 [5] T. Funakoshi T. Tanaka S. Ueda Trans. ISIJ 17 1977 419 427 [6] S. Kanzawa A. Nakajima K. Okamoto K. Kanaya Tetsu-to-Hagané 61 1975 2589 2603 [7] Y. Tomita N. Saito T. Tsuzui Y. Tokunaga K. Okamoto ISIJ Int. 34 1994 829 835 [8] M. Enomoto Met. Mater. 4 1998 115 123 [9] K.M. Wu Y. Inagawa M. Enomoto Mater. Charact. 52 2004 121 127 [10] K.E. Easterling S.A. David Proceedings of an International Conference on Trends in Welding Research ASM Int., Gatlinburg, TN 1986 177 185 [11] K.E. Easterling Introduction to the Physical Metallurgy of Welding 1992 Butterworth-Heinemann London [12] L.E. Svensson Control of Microstructures and Properties in Steel Arc Welding 1994 CRC Press Boca Raton, FL [13] Y. Shi D. Chen Y. Lei X. Li Comput. Mater. Sci. 31 2004 379 388 [14] M.F. Ashby K.E. Easterling Acta Metall. 30 1982 1969 1999 [15] J.C. Ion K.E. Easterling M.F. Ashby Acta Metall. 32 1984 1949 1962