Ag-Doped δ-MnO 2 Nanosheets as Robust Catalysts for Toluene Combustion
Long Zhang,Simin Zhu,Renzhu Li,Wei Deng,Chol Hong,Dongqi Liu,Limin Guo
DOI: https://doi.org/10.1021/acsanm.0c02444
IF: 6.14
2020-12-03
ACS Applied Nano Materials
Abstract:Ag-doped δ-MnO<sub>2</sub> catalysts were synthesized using an alcohol-initiated redox precipitation method at room temperature; toluene was used as a probe molecule of volatile organic compounds (VOCs) to evaluate the catalytic activity of the as-prepared catalyst. The catalytic activity evaluation revealed that the activity for catalytic combustion of toluene was much enhanced by Ag doping. The optimized catalyst (1Ag-MnO<sub>2</sub>) presented the best catalytic activity for toluene combustion, with the conversion of toluene corresponding to 50% (<i>T</i><sub>50</sub>) and 90% (<i>T</i><sub>90</sub>) at just 182 and 190 °C under testing conditions, respectively. In addition, 1Ag-MnO<sub>2</sub> exhibited excellent long-term stability and water resistance. A series of techniques were used to characterize the as-prepared catalysts, and the characterizations demonstrated that the enhanced catalytic performance of Ag-MnO<sub>2</sub> catalysts was closely associated with the much-increased active oxygen species content generated by Ag doping. Therefore, the alcohol-initiated redox precipitation method is a versatile process to prepare Ag-doped MnO<sub>2</sub> catalysts, and the as-prepared Ag-doped MnO<sub>2</sub> catalyst is a robust material for the abatement of toluene.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c02444?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c02444</a>.Detailed procedures for characterizations, XRD patterns, vis–Raman spectra, N<sub>2</sub> sorption isotherms and pore size distributions, TEM mapping images and the EDS spectrum, O<sub>2</sub>-TPD-MS profiles, toluene-TPD profiles, toluene-oxidation TPSR, the supplementary data of toluene oxidation and H<sub>2</sub>-TPR and <i>in situ</i> DRIFTS (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c02444/suppl_file/an0c02444_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology