Potential Utilization of Iron Oxidation Reaction Heat for the Generation of SiO2–FeO System Melts

Rie Endo,Kimia Mitsui,Shota Hashiyama,Leo Miyazaki,Takashi Watanabe,Mitsutoshi Ueda,Miyuki Hayashi,Hiroshi Tanei,Masahiro Susa

DOI: https://doi.org/10.1007/s10765-024-03338-y

2024-02-22

International Journal of Thermophysics

Abstract:Silicon-containing steel forms an oxide layer within the scale during hot rolling. This layer comprising oxides such as Fe 2 SiO 4 and FeO adversely affect the surface quality of steel owing to strong adhesion between Fe 2 SiO 4 and the steel substrate. A method to melt this silicon-containing oxide layer through the oxidation reaction of iron plates by applying SiO 2 powder to the surface is proposed. The aim of this study is to understand the reaction mechanism and identify the optimal conditions for this process. Application of SiO 2 coating to the surface of an iron plate at 6.67 × 10 –4 g·mm −2 and maintaining the plate at 1423 K, just below the eutectic temperature of Fe 2 SiO 4 –FeO system (1450 K), cause the surface oxide scale to melt when exposed to oxidation in an atmospheric environment. Notably, reducing the electric furnace temperature hinders the melting process, whereas excessive application of SiO 2 hampers the formation of sufficient liquid phase. On the surface of the iron plate, primarily FeO and Fe 2 SiO 4 are formed. Heat generation is mainly due to the formation of FeO, which leads to the rapid generation of Fe 2 SiO 4 . Eutectic reactions within SiO 2 –Fe 2 SiO 4 or FeO–Fe 2 SiO 4 systems drive the formation of the liquid phase. Once the liquid phase was established, rapid diffusion of iron ions within it resulted in rapid iron oxidation and additional heat generation. Ultimately, a liquid phase in equilibrium with FeO is formed across the entire surface of the iron plate.

thermodynamics,mechanics,chemistry, physical,physics, applied

What problem does this paper attempt to address?

The paper aims to address the adverse effects of the oxide layer (mainly composed of Fe2SiO4 and FeO) formed during the hot rolling process of silicon-containing steel on the surface quality of the steel. Specifically, the paper proposes a technical method of coating the iron plate surface with SiO2 powder and utilizing the heat generated by the iron oxidation reaction to melt this silicon-containing oxide layer.

### Main Objectives of the Paper:
1. **Understanding the Reaction Mechanism**: Study the oxidation reaction mechanism between SiO2 powder and the iron plate surface.
2. **Determining Optimal Conditions**: Find the optimal process conditions to melt the oxide layer.

### Specific Issues:
- The Fe2SiO4 oxide layer formed during the hot rolling process is difficult to remove due to its strong adhesion to the steel substrate.
- Existing descaling techniques usually require heating the steel plate above the melting point of the oxide layer (approximately 1490 K), but even so, in some cases, the oxide layer is still difficult to completely remove.
- The method proposed in the paper involves coating an appropriate amount of SiO2 powder on the iron plate surface and conducting the oxidation reaction near the eutectic temperature of the Fe2SiO4-FeO system (1450 K) to achieve the melting of the oxide layer.