Abstract:Despite its commercial success, isotactic polypropylene (PP) is not suitable for the applications that require long-term exposure to high-energy conditions, such as elevated temperatures, UV radiation, or high electric fields, due to the combination of polymer chain oxidative degradation, incompatibility with polar additives (antioxidants, stabilizers, etc.), and low material softening temperature. This paper presents a new solution that can simultaneously address both chemical and physical limitations. The idea is to develop a new PP-HP copolymer that contains some specific hindered phenol (HP) groups, homogeneously distributed along the polymer chain. These PP-bound HP pendant groups can not only effectively protect PP chains from the oxidative degradation but also engage in a facile cross-linking reaction to form a 3-D network structure during the oxidation reaction. One accelerated oxidation test in air at 190-210 degrees C shows this distinctive advantage. While a commercial PP polymer (containing common antioxidants and stabilizers) degrades within 1 h, a PP-HP copolymer with about 1 mol % (9 wt %) HP groups shows almost no detectable weight loss after 1000 min. In an ASTM endurance test under a targeted application temperature (140 degrees C in air), the commercial PP shows 1% weight loss within about 10 days. On the other hand, this new PP-HP lasts for 10(5) days (4 order increase) under the same condition. In the strain stress curve measurement, the PP-HP film also shows no detectable change in tensile strength and modulus after constant heating the polymer film at 140 degrees C in air for 1 week. Overall, the experiment results present the potential of expanding PP applications into a much higher temperature range (>140 degrees C) under oxygen oxidative environments.

Improving electric thermal stability of polypropylene by chemically linking small amount of hindered phenol groups

The mechanical properties and thermal performances of polypropylene with a novel intumescent flame retardant

Thermal Stability of Aromatic Polyesters Prepared from Diphenolic Acid and Its Esters

A phosphorus-, nitrogen- and carbon-containing polyelectrolyte complex: preparation, characterization and its flame retardant performance on polypropylene

Increasing Polypropylene High Temperature Stability By Blending Polypropylene-Bonded Hindered Phenol Antioxidant

Synthesis of Functional Polypropylene Containing Hindered Phenol Stabilizers and Applications in Metallized Polymer Film Capacitors

Hindered phenol grafted carbon nanotubes for enhanced thermal oxidative stability of polyethylene

Developing Polypropylene Bonded Hindered Phenol Antioxidants for Expanding Polypropylene Applications in High Temperature Conditions

Polypropylene Copolymer Containing Cross-Linkable Antioxidant Moieties with Long-Term Stability under Elevated Temperature Conditions

Thermal stability and pyrolysis behavior of an efficient fire-retarded polypropylene containing allylamine polyphosphate and pentaerythritol

Polyethylene Containing Antioxidant Moieties Exhibiting High Thermal-Oxidative Stability for High Temperature Applications

Synthesis and thermal decomposition of a novel hyperbranched polyphosphate ester used for flame retardant systems

Preparation of a Novel Stabilizer and Its Thermal‐oxidative Stabilization Effect on Polyamide 6

Mechanical properties and thermal stability of high-temperature (cooking temperature)-resistant PP/HDPE/POE composites

Realizing Simultaneous High‐temperature Strength and Low‐temperature Elongation in Polyolefin Elastomer Toughened Polypropylene Via Controlling the Dispersed Phase Size

Effect of the synergistic interaction of zinc adipate, hydrotalcite and ethylene propylene rubber on the performances of polypropylene

Preparation of an Ionic‐liquid Antistatic/photostabilization Additive and Its Effects on Polypropylene

Crystallization, mechanical, and heat resistance performances of copolymer polypropylene modified by α nucleating agent

Preparation and characterization of high temperature resistant thermosetting polyphenylene ether resin

Crystallization behaviours regulations and thermostability enhancement strategy of polypropylene composites modified by dispersed rice husk charcoal

The Effects of Chemical Structure and Synthesis Method on Photodegradation of Polypropylene