Mechanical properties and thermal stability of high-temperature (cooking temperature)-resistant PP/HDPE/POE composites

Yulong Ma,Kang Yang,Yi Zhang,Juheng Wang,Shu Zeng,Xiaoxiao Huang

DOI: https://doi.org/10.1515/epoly-2023-0164

2024-04-20

e-Polymers

Abstract:The heterogeneous nucleation process of polypropylene (PP)/high density polyethylene (HDPE)/thermoplastic elastomer (POE) composites was realized through blending modification, and characterization techniques, including scanning electron microscopy, differential scanning calorimetry, X-ray diffraction, and dynamic mechanical analysis, were used to analyze the pattern of the impact of modified dicyclohexyl-terephthalamide (TMB-5) on the mechanical properties and thermal stability of the PP/HDPE/POE composites. The results indicated that the modified TMB-5 was advantageous to the improvement of the mechanical properties and thermal stability of the high-temperature (cooking temperature)-resistant PP/HDPE/POE composites. When the amount of added modified TMB-5 was 0.4%, the impact strength and tensile strength of the PP/HDPE/POE composites increased to 36.3 kJ/m 2 and 31.7 MPa, respectively, which were, respectively, 99.5% and 8.5% higher than those of the materials prepared when the amount of added modified TMB was 0.1%. The materials had higher storage modulus in room-temperature and high-temperature environments: 2,438.2 MPa (room temperature), 1,103.9 MPa (120°C), and 1,054.8 MPa (140°C). In addition, the capability of the PP/HDPE/POE composites to crystallize was improved continuously, and the crystallinity increased considerably. At the same time, the crystallization and melting temperatures increased, β-crystal formation was induced, and glass transition temperature increased, thus effectively improving the mechanical properties and thermal stability of the high-temperature (cooking temperature)-resistant PP/HDPE/POE composites.

polymer science

What problem does this paper attempt to address?

The paper mainly addresses the following issues:

1. **Improving the mechanical properties and thermal stability of polypropylene (PP) materials**: Traditional polypropylene materials exhibit poor mechanical properties in high-temperature environments, limiting their application in high-end industrial and agricultural fields, especially in areas requiring high-temperature resistance (cooking temperatures) such as medical materials and sterile packaging for agricultural products.

2. **Developing high-temperature resistant PP composites**: By adding modifiers to improve the overall performance of PP/high-density polyethylene (HDPE)/thermoplastic elastomer (POE) composites, enabling them to maintain good mechanical strength and thermal stability in high-temperature environments.

Specifically, the research achieved heterogeneous nucleation by adding modified dicyclohexyl terephthalamide (TMB-5) as a nucleating agent to PP/HDPE/POE composites, thereby improving the mechanical properties and thermal stability of the composites. Experimental results showed that with an addition amount of 0.4%, the impact strength of the composite reached 36.3 kJ/m², and the tensile strength reached 31.7 MPa, representing increases of 99.5% and 8.5% respectively compared to the addition amount of 0.1%. Furthermore, key properties such as the storage modulus, crystallinity, and melting point of the composites were also significantly enhanced. These improvements enable the composites to be better applied in high-temperature resistant scenarios.