Abstract:Future compact integration of microwave modules will require intermetallic bonding with pitch connections lower than 10 μm. Solid-liquid interdiffusion (SLID) bonding is a potential bonding method for close heterogeneous integration because of its bonding temperature in the range of solder bonding, its ability to withstand higher temperaturs than bonding and its moderate compatibility with the joining of rough surfaces. This paper presents the results of an investigation of the Au—Sn system for integration of A3B5 chips on wafer level using SLID bonding. A sequence of five layers of Au and Sn with weight ratios of about 3:2 was deposited on a sapphire substrate. The structure and phases of the obtained system were investigated before and after annealing. The initial system has five distinctive alternating layers with an overall thickness of around 4.5 μm. After heat treatment at 320 °C with a holding time of 10 minutes, the Au—Sn system transforms into one layer that consists of only one phase ζ (Au0.853Sn0.147). The homogenization process is completed in less than 10 minutes. The ζ phase, of which the system is composed after annealing, has a melting point of 522 °C, which ensures the high temperature stability of the bonding layer. Bonding using the formed system was conducted. Morphology, elemental composition, and the initial mechanical properties of bonded structures have been studied. There are two types of defects in the joint's cross section: voids and the presence of local interfaces between two surfaces (an unbonded-like line). EDX analysis of the cross section of the joint between two crystals shows that the average ratio of Sn to Au over the cross section of the joint is 10.7 %. The complex of studies conducted suggests that the bonding area mostly includes the ζ phase, which will provide the best mechanical strength characteristics among the phases with a high Au concentration. The average bond shear strength is 32 MPa. Initial robustness results of the bonding are promising for space applications.

Hermetic chip-scale packaging using Au:Sn eutectic bonding for implantable devices

Microstructure of AuSn Wafer Bonding for RF-MEMS Packaging

High-Temperature Stable Au–Sn and Cu–Sn Interconnects for 3D Stacked Applications

Low Temperature Au/Sn Solid-Liquid Diffusion Chip-to-Chip Bonding for MEMS Encapsulation

Wafer-Level Au—Sn Solid-Liquid Interdiffusion Bonding for Microwave Applications

Wafer-Level Hermetic Package by Low-Temperature Cu/Sn TLP Bonding with Optimized Sn Thickness

Emerging Encapsulation Technologies for Long-Term Reliability of Microfabricated Implantable Devices

Conformal Hermetic Sealing of Wireless Microelectronic Implantable Chiplets by Multilayered Atomic Layer Deposition (ALD)

A Cu Pillar Bump Bonding Method Using Au-Sn Alloy Cap as the Interconnection Layer

Microstructural Characterization and Mechanical Performance of Wafer-Level SLID Bonded Au-Sn and Cu-Sn Seal Rings for MEMS Encapsulation

Cu–Sn and Ni–Sn transient liquid phase bonding for die-attach technology applications in high-temperature power electronics packaging

The Packaging of Implantable Integrated Sensors

Low-temperature wafer-level bonding with cu-Sn-in solid liquid Interdiffusion for microsystem packaging

Low-Temperature Ultrasonic Bonding of Cu/Sn Microbumps with Au Layer for High Density Interconnection Applications

A novel packaging technology for miniaturization of active long-term implantable medical devices enabling new medical applications

Sn-enhanced high-temperature reliability of Cu/Nano-Ag/Cu joint via transient-liquid-phase bonding

Chronically Implantable Package Based on Alumina Ceramics and Titanium with High-density Feedthroughs for Medical Implants

Ag-Sn Fluxless Wafer Bonding Technology

A Method for Fast Au-Sn Bonding at Low Temperature Using Thermal Gradient

Mechanism and Process of Cu-Sn Bonding for Wafer Level MEMS Packaging

Investigation of Au/Si Eutectic Wafer Bonding for MEMS Accelerometers