Abstract:Statement of problem: Failure of a fiber post and composite resin core often occurs at the junction between the 2 materials. This failure process requires better characterization. Purpose: The purpose of this study was to evaluate the effect of 2 chemical solvents, hydrogen peroxide and methylene chloride, on the shear bond strength of quartz and glass fiber posts to a composite resin. Material and methods: Twenty-four posts (3 +/-0.1 mm in length) were prepared for each quartz (LIGHT-POST (LP)) and glass fiber (Cytec blanco (CB)) post. Posts were horizontally embedded in acrylic resin with half of the post diameter exposed. The exposed surfaces were successively ground with 400-, 800-, and 1200-grit silicon carbide papers, to ensure uniform smoothness. The specimens were divided into 3 subgroups (n=8) representing different surface treatment techniques, including application of silane for 60 seconds (S), etching with hydrogen peroxide for 20 minutes (H), and etching with methylene chloride for 5 seconds (M). Silane-treated specimens served as controls. A dual-polymerized composite resin (Tetric EvoCeram) was placed in a polytetrafluoroethylene mold (30 x 2 mm) positioned upon the post specimens and polymerized for 20 seconds with a light-emitting diode (LED) polymerization unit. The specimens were stored in water at 37 degrees C for 24 hours. Shear bond strength values (MPa) of posts and composite resin cores were measured using a universal testing machine with a crosshead speed of 0.5 mm/min. Data were analyzed by 2-way analysis of variance (ANOVA). Post hoc Tukey intervals for comparison among the 2 post materials and 3 surface treatment techniques were calculated (alpha =.05). The effect of the chemical surface treatments on glass and quartz fiber post surfaces were examined with a scanning electron microscope (SEM). Results: There were significant differences between the shear bond strength for LP and CB (P<.001). For all groups, the application of H showed the highest bond strength values. There was no significant difference between the S and M groups (P>.05). The SEM observations demonstrated that the fiber post surfaces were modified after chemical surface treatment techniques. Conclusions: The surface treatment of quartz and glass fiber posts with hydrogen peroxide significantly enhanced the shear bond strength of the composite resin tested due to its ability to dissolve the epoxy resin matrix used in each post. The lowest bond strength was obtained with M and S groups. Application of methylene chloride to the fiber post surfaces for 5 seconds was not effective in increasing the shear bond strength of the fiber post to composite resin.

Mechanical properties of glass-fibre-reinforced composite posts after laser irradiation with different energy densities

Effect of Irradiation Grafting Epoxy on Surface Characteristics of Carbon Fibers and Mechanical Properties of Composites

Mechanism and Behavior of Laser Irradiation on Carbon Fiber Reinforced Polyetheretherketone (CF/PEEK) During the Laser-Assisted In-Situ Consolidation Additive Manufacturing Process

Flexural modulus, flexural strength, and stiffness of fiber-reinforced posts

The effects of different chemical etching agents on the surface morphology and flexural strength of fiber posts

Effect of Posts Surface Treatments on the Pull-out Bond Strength of Glass Fiber Post to Root Dentin “A Comparative In-Vitro Study”

Surface treatment of glass fiber and carbon fiber posts: SEM characterization

Infrared Laser Heating of GFRP Bars and Finite Element Temperature Field Simulation

Effect of Laser Surface Treatment on Surface and Bonding Properties of Carbon Fiber Reinforced Composites

Effect of Co60gamma Ray Irradiation for Carbon Fibre on Interfacial Properties in Epoxy Resin Composites

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Flexural Strength of Dental Fiber Composite Post Manufactured with a Novel Approach

Effects of chemical surface treatments of quartz and glass fiber posts on the retention of a composite resin

Bending properties of glass fiber-reinforced plastic for post materials evaluated by cantilever test

Effect of femtosecond laser induced surface patterns on the flexural strength of monolithic zirconia

The Effect of Fiber Position and Polymerization Condition on the Flexural Properties of Fiber-Reinforced Composite

Effects of Er,Cr:YSGG Laser Surface Treatments and Composites with Different Viscosities on the Repair Bond Strength of CAD/CAM Resin Nanoceramic

[Effects of Femtosecond Laser Treatment on Surface Characteristics and Flexural Strength of Zirconia].

Effects of various laser applications on surface roughness and bond strength to veneering composites of polyether ether ketone (PEEK) and polyether ketone ketone (PEKK) materials

Effects of laser modalities on shear bond strengths of composite superstructure to zirconia and PEEK infrastructures: an in vitro study

Effects of Different Surface Treatments of Woven Glass Fibers on Mechanical Properties of an Acrylic Denture Base Material