Abstract:CoCrFeNi alloy is the most well-known four-component equiatomic alloy. In addition, it has a low-cost composition among HEAs. Four-component alloys are considered semi-HEAs. Therefore, a five-component HEA design was made by adding another metal to the main composition of CoCrFeNi. As the fifth metal, two metals such as Al and Ti, which are relatively low in cost and have the potential to improve properties, were chosen. For this purpose, in this study, the effect of Al and Ti on CoCrFeNi main alloy was investigated by producing three different samples as CoCrFeNi, CoCrFeNiAl, and CoCrFeNiTi. The alloys with three different compositions (used three different samples) were successfully produced by the mechanical alloying method. Although Al and Ti have the possibility of intermetallic with other metals in the alloy, such a formation was not observed during mechanical alloying, and it was observed that all metals were homogeneously distributed in the alloy. The microhardness results indicated that CoCrFeNiAl and CoCrFeNiTi samples had similar hardness values. While the hardness of the CoCrFeNi sample was 136 HV, the hardness of the CoCrFeNiAl sample was 262 HV. However, the hardness of the CoCrFeNiTi sample decreased significantly. The hardness of the CoCrFeNiTi sample was measured as 269 HV. It was observed that the addition of Ti and Al to the base alloy was increased a significant change in hardness. It has been observed that Ti supplementation has a more positive effect on improving corrosion properties. It is seen that the corrosion potentials shift toward more negative potentials with the addition of Al and Ti to the CoCrFeNi (−194 mV) alloy (−306 and −224 mV for CoCrFeNiAl and CoCrFeNiTi, respectively). When the surface morphologies of the alloys are compared after corrosion; the damage to the alloy surfaces increases due to the negative E corr value in CoCrFeNiAl and CoCrFeNiTi alloys compared to the master alloy. However, the high corrosion current density (12.69 μA/cm 2 ) in the CoCrFeNiTi sample caused much more damage to this alloy.

Synthesis of Equiatomic CoCrFeMnTiNi Multicomponent Alloy by Sequential Alloying Using Mechanical Alloying and Vacuum Arc Melting

Evaluation of Equiatomic CrMnFeCoNiCu System and Subsequent Derivation of a Non-Equiatomic MnFeCoNiCu Alloy

Design Multicomponent Eutectic Alloys in the Co–Cr–Fe–Ni–Nb System Using Simple Mixing Method

Competition Between Elements During Mechanical Alloying in an Octonary Multi-Principal-element Alloy System

Alloying behavior of binary to octonary alloys based on Cu–Ni–Al–Co–Cr–Fe–Ti–Mo during mechanical alloying

Microstructure and mechanical properties of non equiatomic FeCoNiCuMo high entropy systems

Mechanical Alloying Behavior and Thermal Stability of CoCrCuFeMnNix High-Entropy Alloy Powders Prepared via MA

Design of synergistic alloying CoCrFeNi eutectic high entropy alloy based on infinite solid solution

Microstructure characterization and phase evolution of equiatomic AlCoMoFeNi high entropy alloy synthesized by mechanical alloying

Microstructural and Magnetic Characteristics of High-Entropy FeCoNiMnTi Alloy Produced via Mechanical Alloying

A novel alloy design for non-equiatomic high-entropy alloy (Cr–Fe–Ni–Ti–Nb): predicting entropy mix and enthalpy mix

Microstructural evolution and phase selection during solidification of AlCrCuFeNi high entropy alloy

Microstructure and mechanical properties of a high entropy alloy with a eutectic composition (AlCoCrFeNi2.1) synthesized by mechanical alloying and spark plasma sintering

Is synthesizing a Cu35Co35Ni20Ti5Al5 high-entropy alloy beyond the rules of solid-solution formation?

Synthesis of a single phase of high-entropy Laves intermetallics in the Ti–Zr–V–Cr–Ni equiatomic alloy

Production of CoCrFeNi(Al/Ti) High-Entropy Alloys by Mechanical Alloying: Optimization of Milling Time and Comparison of Corrosion Susceptibilities

Phase Evolution and Mechanical Properties of AlCoCrFeNiSix High-Entropy Alloys Synthesized by Mechanical Alloying and Spark Plasma Sintering

Combinatorial Alloy Design and Microstructure Evolution in Laser-cladded Al–Co–Cr–Fe–Ni–Ti Compositionally Complex Alloys

Effect of Mechanical Alloying on the Microstructure of CoCrNiTiMox High Entropy Alloy

Nanostructured Al–Ti–Fe–Mn–Ni High-Entropy Alloy by Mechanical Alloying: Synthesis and Characterization

Mechanical Alloying with the Partial Amorphization of the Fe–Cr–Co–Ni–Mn Multicomponent Powder Mixture and Its Spark Plasma Sintering to Produce a Compact High-Entropy Material