Abstract:The functionalization of Miscanthus x giganteus stems fragments (R-MSF) by dimethyl(methacryloyloxy)methyl phosphonate (MAPC1) using pre-irradiation was studied. The influence of the composition and the structure of the substrate on the grafting efficiency was investigated by comparing the results with short flax fibers (SFF) and bleached Miscanthus x giganteus stems fragments (B-MSF). The lignocellulosic substrates were irradiated at several target doses ranging from 11 to 108.1 kGy using e-Beam. Electron Paramagnetic Resonance spectroscopy (EPR) highlighted major differences in terms of radical nature between R-MSF, SFF, and B-MSF samples. Following the polymerization reactions, washing, and drying steps, the phosphorus contents were measured by X-ray fluorescence spectrometry (XRF). Unlike Flax, pre-irradiation grafting was not efficient on R-MSF. The role of lignin content on grafting reactions was then evaluated by comparing R-MSF with SFFand B-MSF), showing only a minor impact. Using a reducing agent, it was possible to reach a phosphorus content of about 1.4 wt% for R-MSF and up to 4.0 wt% for B-MSF for a 100 kGy dose. Furthermore, phosphorus mapping using scanning electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM-EDX) highlighted a homogeneous dispersion of the grafted macromolecules. This demonstrates the possibility of conducting pre-irradiation grafting on lignin-rich substrates without bleaching. Efforts were then made to optimize the operating conditions in terms of storage temperature, reaction temperature and Fe 2+ concentration. Finally, the fire behavior of treated Miscanthus x giganteus stem fragments was evaluated by pyrolysis-combustion flow calorimetry (PCFC).

Preparation and Characterization of Glycidyl Methacrylate (GMA) Grafted Kapok Fiber by Using Radiation Induced-grafting Technique

Effect of Irradiation Grafting Epoxy on Surface Characteristics of Carbon Fibers and Mechanical Properties of Composites

Bulk Graft Modification of Polyolefin Membranes by Combining Pre-Irradiation-Induced Graft and Supercritical Co2-Swelling Polymerization

Modification of microcrystalline cellulose by gamma radiation-induced grafting

Functionalization of Carbon Nanotubes by Corona‐Discharge Induced Graft Polymerization for the Reinforcement of Epoxy Nanocomposites

Synthesis and Characterization of Cation-Exchange Fibers with Radiation-Induced Grafting of Glycidyl Methacrylate onto Cotton Cellulose

Pre-irradiation Grafting of Temperature Sensitive Hydrogel on Cotton Cellulose Fabric

Poster Presentation : 2P-35 ; Grafting polymerization of GMA onto cellulose by E-beam radiation and preparation of ion exchange fiber

Improving the compatibility, surface strength, and dimensional stability of cellulosic fibers using glycidyl methacrylate grafting

Microwave induced synthesis of graft copolymer of binary vinyl monomer mixtures onto delignified Grewia optiva fiber: application in dye removal

STUDY ON PRE-IRRADIATION GRAFTING OF NIPAAm ONTO COTTON CELLULOSE FABRIC

Grafting of glycidyl methacrylate onto polycaprolactone: preparation and characterization

Effect of Γ-Ray Irradiation Grafting on the Surface Property and the Bulk Structure of M40J Fiber

Surface Graft Polymerization of Glycidyl Methacrylate Onto Polyethylene and the Adhesion with Epoxy Resin

Gamma radiation-assisted functionalization of flax fibers for diversified applications

Grafting Polymerization of Acrylic Acid Onto Preirradiated Polypropylene Fabric

Radiation Grafting Of Binary Monomers Onto Cotton Cellulose

Fabrication of Glycidyl Methacrylate (GMA) Grafted Cellulose from Rice Straw

Grafting copolymerization of N,N-dimethyacrylaminoethylmethacrylate (DMAEMA) onto preirradiated polypropylene films

Surface grafting modification of carbon fibers by γ-ray pre-irradiation and plasma technique

Radiation-induced graft copolymerization of a phosphonate monomer onto short flax fibers and Miscanthus x giganteus stem fragments: Influence of substrate composition