A comparative study of smart polyurethane foam using RSM and COMSOL multiphysics for acoustical applications: from materials to component
Vinoth Kumar Selvaraj,Jeyanthi Subramanian
DOI: https://doi.org/10.1007/s10934-022-01362-7
2022-10-13
Journal of Porous Materials
Abstract:A biodegradable, lightweight, and flexible smart PU foam was manufactured using absorption and hydrothermal reduction process and tested for its acoustic properties per ASTM standard E 1050-12. The nanoparticles used in this research are graphene (Gr), zirconium oxide (ZrO 2 ), and bamboo charcoal (BC). The foam's structure and the uniform distribution of its nanoparticles were seen using FESEM, and the FTIR graph was used to identify the carbon compounds present in the foam. According to the Johnson-Champoux-Allard-Lafarge model, the five important characteristics such as porosity, airflow resistivity, tortuosity, viscous, and thermal characteristic length were determined from the sound absorption coefficient (SAC) using inverse acoustical characterization through MATLAB. The composition of nanoparticles in different foams was consistently designed using central composite design (CCD). Through response surface methodology (RSM), the optimum weight% of nanoparticles was analyzed to produce the maximum noise reduction coefficient (NRC). The maximum value of NRC obtained is 0.628 for the optimal weight percentages of 0.1 wt% of Gr, 0.1 wt% of ZrO 2 , and 2.5 wt% of BC. The evaluation of experimental results of sound absorption coefficient was compared with inverse characteristics using Matlab code and with simulation using Comsol Multiphysics 5.5. The SPL plot shows an average 5 to 31 dB SPL reduction for the best sample (A8). The outcome suggests that the smart composite foam could be an excellent material for sound insulation for automobiles, building walls, machinery, and aircraft applications.
materials science, multidisciplinary,chemistry, physical, applied