Abstract:The radial structure of polyacrylonitrile fibers oxidized before carbonization and its distribution directly affect the performance of the resulting carbon fibers. Optimizing the radial distribution of the oxidized structure and establishing a relationship between this structure and the mechanical properties of the final carbon fibers will help optimize the oxidation conditions for the preparation of high-performance carbon fibers. Solid-state nuclear magnetic resonance spectroscopy, optical microscopy, thermogravimetric analysis, and mechanical tests were used to investigate the effect of the oxidation reaction rate on the radial distribution of the structure of the oxidized fibers and the mechanical properties of the resulting carbon fibers. The oxidation reaction rates were controlled by regulating the oxidation temperature gradient. Results show that the degree of oxidation increases with both the average and initial oxidation rates. By increasing the average oxidation reaction rate, the oxidized structure penetrates deeper into the core region of the fibers, the content of oxygen-containing functional groups increases, the thermal stability of the fibers decreases, and the degree of graphitization of the final carbon fibers increases, but the density of the fibers is decreased and their mechanical properties are degraded. Compared with sample obtained with the lower initial oxidation rate, the number of oxygen-containing functional groups, thermal stability, degree of graphitization and density of the final carbon fibers of the sample with the higher initial oxidation rate are higher, and its tensile strength and modulus are respectively 4.2% and 2.2% higher. A new type of carbon fiber with high strength, medium modulus and a relatively large diameter is obtained under the optimized oxidation conditions.

Study on Structure Evolution and Reaction Mechanism in Microwave Pre-oxidation

Microwave Treatment of Pre-Oxidized Fibers for Improving Their Structure and Mechanical Properties

Microwave-Assisted Oxidative Degradation of Lignin Model Compounds with Metal Salts

Comparative Study of Conventional and Microwave Heating of Polyacrylonitrile-Based Fibres

Microwave Heating and Devolatilization Characteristics of Polyethylene Particles in a Fixed‐bed Devolatilizer

Study on preparation of high cyclization degree and high strength pre-oxidized fiber by nitration

A Two-Step Microwave Annealing Process for PAN Pre-Oxidation through a TM-Mode Cavity

Study on the post-irradiation oxidation of polyethylenes using EPR and FTIR technique

Chemical Structure Evolution and Mechanism During Pre-Carbonization of PAN-based Stabilized Fiber in the Temperature Range of 350–600 °C

Effect of Granularity on Pretreatment of Coke with Microwave Irradiation

Evolution mechanism of cyclized structure of PAN-based pre-oxidized fiber during low temperature carbonization process

EFFECT OF MICROWAVE IRRADIATION ON GRAPHITIZATION OF CARBON MATRIX IN PULVERIZED COAL

Evolution and Regulation of Radial Structure of PAN Pre-Oxidized Fiber Based on the Fine Denier Model

An investigation into the modification of microwave-assisted oxidation in the macromolecular structure of coal via XRD and Raman spectroscopy

Effect of oxygen content on the preoxidation structure of polyacrylonitrile fibers

Regulating the radial structure of polyacrylonitrile fibers during pre-oxidation and its effect on the mechanical properties of the resulting carbon fibers

Effect of pre-oxidation temperature and heating rate on the microstructure of lignin carbon fibers

The mechanism of de-SO2and De-NOx with solid waste by microwave effect

Radiation assisted pre-oxidation of polyacrylonitrile fiber: Graphite formation and lower crystal size revealed by 2D WAXD at a synchrotron facility

Study on the structural evolution of polyacrylonitrile fibers in stepwise heat treatment process and its relationship with properties

Microwave heating oxidative stabilization of KMnO4 modified polyacrylonitrile-based carbon fiber precursor