Theoretical Examination of the Radiation Shielding Qualities of MgO-PbO-SiO2-B2O3-BaO Glass Systems

M. I. Sayyed

DOI: https://doi.org/10.1007/s12633-024-02914-z

IF: 3.4

2024-02-16

Silicon

Abstract:Melt quenching method was used to prepare a glass series composed of 5MgO-20PbO-10SiO 2 -(65-x)B 2 O 3 -xBaO, (x = 10, 15, 20 and 25 mol%), with the resulting glasses' capacity for radiation shielding explored through Phy-X software. The mass attenuation coefficients (MAC) were examined in the 0.122–1.485 MeV energy range, with 0.122 MeV the resulting maximum value and a 1.557–1.611 cm 2 /g variation. At the low energy range, a clear relationship between the MAC and the energy emerged, with 0.054 cm 2 /g at 0.122 MeV representing the MAC difference between the lowest and highest BaO-content glasses. Conversely, at the high energy range, the influence of BaO on the MAC diminished considerably, whereby the MAC difference between the two glasses was a mere 0.001. We evaluated the prepared glasses' linear attenuation coefficients (LAC), finding a direct relation between the LAC and glass density. At 0.245 MeV, the LAC values were 1.425, 1.486, 1.546, and 1.607 cm −1 at the respective densities of 4.275, 4.438, 4.601, and 4.764 cm −1 . According to the LAC results, the glass with the composition of 5MgO-20PbO-40 B 2 O 3 -10SiO 2 -25BaO has the more desirable shielding properties. We observed a decrease in the TF with increasing the amount of BaO in the prepared glasses. This observation implies that BaO has an important role in enhancing the glasses' radiation shielding ability.

materials science, multidisciplinary,chemistry, physical