Mechanical and Radiation Shielding Study of B2O3–SiO2–P2O5–Li2O –TiO2 Glasses

Eman M. Mahrous,Ateyyah M. Al-Baradi,Kh. S. Shaaban

DOI: https://doi.org/10.1007/s11665-024-10332-w

IF: 2.3

2024-11-17

Journal of Materials Engineering and Performance

Abstract:40B 2 O 3 -20SiO 2 -20P 2 O 5 -( 20-x ) Li 2 O- x TiO 2 glasses containing B 2 O 3 ,SiO 2 ,P 2 O 5 ,Li 2 O and variable amounts of TiO 2 were formed using the melt-quenching procedure. The absence of Bragg's peaks suggested that every sample was amorphous in XRD spectra. The increase in density, ultrasonic velocity, and elastic moduli of the glass samples as the TiO 2 level increases suggests the formation of a more expanded structure with greater TiO 2 content. Both the ultrasonic velocity ( ) and shear ( ) have increased. ( ) increased from 5070 to 5495 m/s, whereas ( ) increased from 2890 to 3080 m/s. The elastic moduli of the glasses have increased as the concentration TiO 2 increased. Including TiO 2 in B 2 O 3 –SiO 2 –P 2 O 5 –Li 2 O glasses and investigating its impact on gamma shielding properties through Phy-X simulation provides valuable insights into the glass's performance in radiation protection. Including TiO 2 enhances the proficiency of the shielding due to its influence on the MAC, resulting in better absorption of radiation and hence lower HVL values. The composition-dependent elastic properties of B 2 O 3 –SiO 2 –P 2 O 5 –Li 2 O–TiO 2 glasses have significant implications for their potential practical applications.

materials science, multidisciplinary