Abstract:A transverse grain boundary perpendicular to the applied loading direction is normally considered a main reason for the deterioration of the mechanical properties of nickel-based superalloys at high temperatures. Therefore, reducing or even eliminating these types of grain boundaries can effectively delay failure and improve high-temperature mechanical properties. In this study, the feasibility of process parameter optimization and substrate rotation was explored for fabricating single-crystal Inconel 718 specimens during laser directed energy deposition (LDED). The study determined that optimizing the process parameters was dependent on the ability to enlarge the [001] region at the bottom of the melt pool as much as possible. Simultaneously, ensuring that the remelting depth exceeded the stray grain region height at the top of the melt pool was necessary. Therefore, that the stray grains can be fully erased during the subsequent deposition process. Accordingly, an Inconel 718 single-walled specimen (height: 20mm) with a full single-crystal structure was successfully fabricated using LDED for the first time. However, this approach remains insufficient for fabricating a block with a single-crystal structure, as SGs appear readily in the overlapping regions. Substrate rotation was further considered, where ensuring that one side of the melt pool was in the [001]-grain region was critical. Although the other side of the melt pool featured SGs, they were eliminated through the following overlapping process, as the SG region in the current melt pool corresponded to the [001]-grain region in the next melt pool. Through these two approaches, a small-format single-crystal block with dimensions of 27 × 8.3 × 1.3mm (length × width × height) was successfully fabricated. Because the Inconel 718 superalloy is not specifically designed for single-crystal structure generation, a large-format block with a single-crystal structure still cannot be fabricated using these approaches. Nevertheless, the findings remain insightful because they demonstrate a wider range of variable microstructures achievable with additive manufacturing processes than with traditional forming processes such as casting or forging and may provide more opportunities for improving the mechanical properties. In addition, the preparation of a small-format single-crystal structure has significant applications in repairing damaged components such as aeroengine blades.

Study of the Microstructures and Fatigue–Creep Properties of a Laser-Directed Energy Deposition Epitaxial Ni-Based Superalloy

Mechanism of High Temperature Mechanical Properties Enhancement of Ni-based Superalloys Repaired by Laser Directed Energy Deposition: Microstructure Analysis and Crystal Plasticity Simulation

Influence of Γ/γ′ Morphology Evolution on the Mechanical Properties of Ni-based Single Crystal Superalloys Formed by Laser Metal Deposition

A Synchrotron Study of Microstructure Gradient in Laser Additively Formed Epitaxial Ni-based Superalloy

The Microstructure Characteristic and Its Influence on the Stray Grains of Nickel-based Single Crystal Superalloys Prepared by Laser Directed Energy Deposition

Regulation of Microstructure, Phase Transformation Behavior, and Enhanced High Superelastic Cycling Stability in Laser Direct Energy Deposition NiTi Shape Memory Alloys Via Aging Treatment

Microstructural Evolution and Its Influence on the Wear Resistance of a Laser Directed Energy Deposited Ni-based Single Crystal Superalloy

Microstructure and fracture behavior of 90W-7Ni-3Fe alloy fabricated by laser directed energy deposition

Microstructure and mechanical properties of laser-assisted epitaxial growth of nickel-based single crystal superalloys

The microstructural evolution and mechanical response of laser direct energy deposition Inconel 718 alloy based on simulation and experimental methods

Effect of thermal cycles on laser direct energy deposition repair performance of nickel-based superalloy: Microstructure and tensile properties

Microstructure and Fatigue Crack Growth Behavior of Inconel 718 Superalloy Fabricated Via Laser Directed Energy Deposition Additive Manufacturing

Improved High-temperature Fatigue Performance of Laser Directed Energy Deposited Ni-based Superalloy by Regulating the Heat Treatment

Hot Workability and Microstructural Evolution of a Nickel-Based Superalloy Fabricated by Laser-Based Directed Energy Deposition

Single-crystal Structure Formation in Laser Directed Energy Deposited Inconel 718 Through Process Parameter Optimization and Substrate Orientation Tuning

Microstructure evolution and formation mechanism of a crack-free nickel-based superalloy fabricated by laser engineered net shaping

Microstructural characterization and fatigue performance of the recast material induced by laser manufacturing of a nickel-based superalloy

Microstructure and Nanoindentation Creep Behavior of IC10 Directionally Solidified Superalloy Repaired by Laser Metal Deposition

Study on the anisotropic high cycle fatigue performance of L-DEDed Ni-based superalloy: Microstructure, failure mechanism and fatigue limit evaluation

Microstructure and Fatigue Crack Growth Behavior of Inconel 718 Superalloy Manufactured by Laser Directed Energy Deposition

Microstructural Deformation Behavior of Laser Shock Peening Ni Alloys: Experimental and Molecular Dynamics Simulation Investigations